1) water borne inorganic zinc-rich coatings
水性无机富锌涂料
1.
are added in ordinary water borne inorganic zinc-rich coatings,Organic filming basal material and corrosion retarding material,so that the construction adaptability of water borne inorganic zinc-rich coatings is greatly expanded,the adhesion of the coating,compactness,anti-ager and anti-slippery performance are remarkablely improved.
在常见的水性无机富锌涂料中,添加有机成膜基料和缓蚀性材料,使水性无机富锌涂料的施工适应性大大拓宽,改善了涂膜的附着性、致密性、耐老化性和抗滑移性。
2) waterborne inorganic zinc silicate coating
水性无机硅酸富锌涂料
3) inorganic zinc-rich coatings
无机富锌涂料
1.
Through application of frankincense resin in epoxy coatings,inorganic zinc-rich coatings and acrylic coatings.
分析了乳香树脂的结构和性能,通过其在环氧涂料、无机富锌涂料和丙烯酸涂料的应用研究,发现乳香树脂能够提高涂料的机械性能和耐腐蚀性能。
2.
In view of environmental protection, water-borne inorganic zinc-rich coatings, especially for whose binder used is potassium silicate solutions, become one of the most hopeful categories available today in the field of heavy-duty anticorrosion, for its cheap cost and outstanding performance.
随着人们环保意识的逐渐增强,水性无机富锌涂料,尤其是以硅酸钾水溶液为基料的富锌涂料,以其廉价的成本和优异的性能已成为环保型重防腐涂料中最重要的品种之一。
4) inorganic waterborne zinc silicate paintganic paint
水性无机硅酸锌涂料
6) zinc-rich coatings
富锌涂料
1.
The paper introduced the characteristics of several zinc-rich coatings anti the method of zinc content measurement.
介绍了几种富锌涂料的特点及其锌含量的测定方法。
2.
This paper introduces new development trend of overseas zinc-rich coatings preparation with zinc flake instead of spherical zinc powder and discusses the anticorrosion mechanism of flake zinc-rich coatings film.
介绍了国外采用鳞片状锌粉取代球状锌粉研制富锌涂料发展的新趋势,对鳞片状锌基涂层抗蚀性能的机理进行了探讨,并从实际实验数据中得到了与理论分析相一致的结论,即鳞片状锌粉涂层在干膜含锌量降低的情况下,其抗蚀性能仍优于球状锌粉涂层,鳞片状富锌涂料是球状富锌涂料理想的换代产品。
3.
The formulation of high mole ratio potassium silicate zinc-rich coatings is given, which is compared to the similar products abroad in terms of its performance.
研究了不同硅溶胶、硅酸钾和烷氧基硅烷对高模数硅酸钾制备的影响 ;探讨了温度、时间和搅拌速度对高模数硅酸钾制备的影响 ;进行了高模数硅酸钾富锌涂料的配方实验 ,并与国外样品的性能进行了比较。
补充资料：无机富锌车间底漆
分子式：
CAS号：
性质：此类涂料主要由基料、锌粉、着色颜料、填充料和添加剂等组成。基料起黏结锌粉的作用，主要品种有硅酸烷基酯、硅酸烷基酯/钛酸烷基酯、硅酸烷基酯/硼酸烷基酯及其他改性品种。锌粉一般用超细锌粉，颗粒度0.2～12μm，平均粒度5μm，用量50％～80％。施工干膜厚一般20μm左右，兼具电化学保护和化学防蚀双重作用。户外耐久性可达6～8个月，适用于周期较长、防腐蚀要求较高的场合(如造船业防腐)。
CAS号：
性质：此类涂料主要由基料、锌粉、着色颜料、填充料和添加剂等组成。基料起黏结锌粉的作用，主要品种有硅酸烷基酯、硅酸烷基酯/钛酸烷基酯、硅酸烷基酯/硼酸烷基酯及其他改性品种。锌粉一般用超细锌粉，颗粒度0.2～12μm，平均粒度5μm，用量50％～80％。施工干膜厚一般20μm左右，兼具电化学保护和化学防蚀双重作用。户外耐久性可达6～8个月，适用于周期较长、防腐蚀要求较高的场合(如造船业防腐)。