您的位置:首页 -> 词典 -> Nd修饰CexZr1-xO2(x=0.8,0.6,0.2)固溶体
1)  CexZr1-xO2(x=0.8,0.6,0.2) solid solutions modified with Nd
Nd修饰CexZr1-xO2(x=0.8,0.6,0.2)固溶体
2)  Ce xZr 1-xO 2 solid solutions
CexZr1-xO2固溶体
3)  ZrxCe1-xO2solid solution
ZrxCe1-xO2固溶体
4)  Ce_xTh_(1-x)O_2 solid solution
CexTh1-xO2固溶体
1.
Ce_xTh_(1-x)O_2 solid solutions were prepared by sol-gel method, and their structure and reduction properties were studied.
采用柠檬酸法制备了CexTh1-xO2固溶体,并对固溶体的结构和还原性能进行了表征。
5)  CexPd1-xO2-δ solid solution
CexPd1-xO2-δ固溶体
1.
Results of XRD indicated that CexPd1-xO2-δ solid solution was formed when the catalysts were calcined at 400-800 ℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000 ℃).
XRD结果表明,焙烧温度从400℃升高到800℃,有利于CexPd1-xO2-δ固溶体的形成。
6)  mesoporous CexZr1-xO2
介孔CexZr1-xO2
1.
The mesoporous CexZr1-xO2 oxide was successfully synthesized by polyol method.
采用多元醇法合成了介孔CexZr1-xO2(x=0。
补充资料:airedale violet nd
CAS:2586-60-9
分子式:C32H22N6Na2O8S2
分子质量:728.69
中文名称:直接紫N;直接青莲N;直接紫 N;直接青莲 N
英文名称:Direct violet N;C.I. Direct violet 1;airedale violet nd;amanil fast violet n;atlantic violet n;atul direct violet n;azocard violet n
性状描述:红褐色粉状物。溶于水呈深枣红色至紫色,也溶于溶纤素,不溶于其他有机溶剂,微溶于乙醇呈红光紫色。遇浓硫酸呈深蓝色,稀释后旦暗紫色;遇浓硝酸呈红棕色。其水溶液加浓盐酸有紫色沉淀,加浓氢氧化钠液有紫酱色沉淀,用于对纤维素类纤维染色时,染料吸尽性好,温度在100℃亲合力最大。
生产方法:由联苯胺重氮化后与γ酸进行偶合,再经盐析;过滤及干燥而得。原料消耗(kg/t)联苯胺(100%) 100γ酸 260纯碱(工业) 35氢氧化钠(100%) 65亚硝酸钠 80盐酸(31%) 190碳酸氢钠 110乙酸钠(58-60%) 50元明粉 100
用途:该品主要用于棉;粘胶等纤维素纤维和染色,也可用于蚕丝;锦纶及锦/粘混纺织物的染色,还可用于皮革;纸张和生物的染色。该品用于棉;粘胶织物染色后,经脲醛树脂整理,色泽显著转蓝,经固色剂M处理,色泽显著转黄。该品还可用于棉;粘胶织物的直接印花,也可作拔染印花的地色。该品色光鲜艳,用途广,除单独使用外,常与直接红;蓝;棕;灰等染料拼色。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条