1) Ca_(2-x)Sr_xZn_4Ti_(15)O_(36) solid solution
Ca_(2-x)Sr_xZn_4Ti_(15)O_(36)固溶体
2) Ce_xPd_(1-x)O_(2-δ) solid solution
Ce_xPd_(1-x)O_(2-δ)固溶体
1.
XRD results indicated that a Ce_xPd_(1-x)O_(2-δ) solid solution was formed when the catalysts were calcined at 400-800℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000℃).
XRD实验结果表明,焙烧温度从400℃升高到800℃,有利于催化剂中Ce_xPd_(1-x)O_(2-δ)固溶体的形成,然而焙烧温度升至1000℃时,导致Pd物种从固溶体中析出。
3) Mn(Cu)_(0.1)Ce_(0.9)O_(2-δ) Solid Solution
Mn(Cu)_(0.1)Ce_(0.9)O_(2-δ)固溶体
4) Ce 0.9 Ca 0.1 O 2-δ particles
Ce_(0.9)Ca_(0.1)O_(2-δ)颗粒
5) BaZn_(2-x)Ni_xFe_(16)O_(27) ferrite
BaZn_(2-x)Ni_xFe_(16)O_(27)铁氧体
6) solid solution Ce_(1-x)Nd_xO_(2-δ)
固溶体Ce_(1-x)Nd_xO_(2-δ)