1) solid solution Ce_(1-x)Nd_xO_(2-δ)
固溶体Ce_(1-x)Nd_xO_(2-δ)
2) Ce_(1-X)Cu_XO_Y solid solution
Ce_(1-X)Cu_XO_Y固溶体
3) Ce_(0.6)Zr_(0.4-x)Pr_xO_(2-δ) solid solution
Ce_(0.6)Zr_(0.4-x)Pr_xO_(2-δ)固溶体
4) Ce_xPd_(1-x)O_(2-δ) solid solution
Ce_xPd_(1-x)O_(2-δ)固溶体
1.
XRD results indicated that a Ce_xPd_(1-x)O_(2-δ) solid solution was formed when the catalysts were calcined at 400-800℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000℃).
XRD实验结果表明,焙烧温度从400℃升高到800℃,有利于催化剂中Ce_xPd_(1-x)O_(2-δ)固溶体的形成,然而焙烧温度升至1000℃时,导致Pd物种从固溶体中析出。
5) Mn(Cu)_(0.1)Ce_(0.9)O_(2-δ) Solid Solution
Mn(Cu)_(0.1)Ce_(0.9)O_(2-δ)固溶体
6) Ce 1-x Y x Fe 2
Ce_(1-x)Y_xFe_2
补充资料：插入固溶体
分子式：
CAS号：
性质：又称插(嵌)入固溶体.若干溶质质点嵌入固相溶剂质点的间隙中而构成的固溶体。通常，插入溶质的半径与溶剂质点的半径相比特别小时易于形成。在金属键的物质中这类固溶体很普遍，添入的氩、碳、硼都容易处在这些晶格的间隙位置中。如碳溶入v-铁中形成的间隙固溶体称为奥氏体。间隙固溶体的形成常有助于晶体的硬度、熔点和强度的提高。
CAS号：
性质：又称插(嵌)入固溶体.若干溶质质点嵌入固相溶剂质点的间隙中而构成的固溶体。通常，插入溶质的半径与溶剂质点的半径相比特别小时易于形成。在金属键的物质中这类固溶体很普遍，添入的氩、碳、硼都容易处在这些晶格的间隙位置中。如碳溶入v-铁中形成的间隙固溶体称为奥氏体。间隙固溶体的形成常有助于晶体的硬度、熔点和强度的提高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。