1) Mo2FeB2-based cermet
Mo2FeB2基金属陶瓷
1.
Using Mo,Fe,FeB,Cr,Ni and C powders as raw materials,Mo2FeB2-based cermet was prepared by reaction sintering.
以Mo、Fe、FeB、Cr、Ni、C为原料,采用反应烧结法制备Mo2FeB2基金属陶瓷。
2.
Using Mo, Fe, FeB and Mn powders as raw materials, Mo2FeB2-based cermet was prepared by reaction sintering process.
以Mo、Fe、FeB和Mn等为原料,采用反应烧结法制备Mo2FeB2基金属陶瓷。
2) Mo2FeB2 cermet
Mo2FeB2金属陶瓷
1.
Mo2FeB2 cermet-steel clad materials are prepared via slip forming technique with FeB,Mo and Fe powders taken as raw materials.
以FeB,Mo,Fe等粉末为主要原材料,加入有机溶剂,制备出成型料浆,用料浆法在钢基体表面成型覆层坯体,采用真空液相烧结技术,制备了Mo2FeB2金属陶瓷-钢覆层材料,并对其性能进行了检测。
3) Ti(CN) based ceramets
Ti(CN)金属基陶瓷
4) TiC-based cermets
TiC基金属陶瓷
1.
Three series of cermets such as TiC-ZrC-10Co-10Ni-1C,TiC-ZrC-14Mo-20Ni-1C and TiC-ZrC-14Mo-15WC-20Ni-1C were fabricated by vacuum sintering in order to study the effect of ZrC on the properties of TiC-based cermets.
为研究ZrC对TiC基金属陶瓷性能的影响,真空烧结制备了TiC-ZrC-10Co-10Ni-1C、TiC-ZrC-14Mo-20Ni-1C、TiC-ZrC-14Mo-15WC-20Ni-1C系金属陶瓷。
2.
TiC-based cermets have been widely used as a tool material in mechanical processing owing to its outstanding physical, mechanical and wear-resistant properties.
TiC基金属陶瓷具有优良的物理、力学性能和耐磨性能，因而被广泛用作机械加工中的工具材料。
5) metal-base ceramics
金属基陶瓷内衬
补充资料：钼基金属陶瓷
分子式：
CAS号：
性质：以难熔金属钼为基添加氧化物烧结成的材料。钼和钼合金与氧化锆、氧化铝等制取的金属陶瓷，具有熔点高、抗氧化性好、耐熔渣腐蚀、抗热震、抗磨等的优点。钼基金属陶瓷热电偶护管阳最高使用温度在还原与真空气氛中可这1700℃，与钨铼热电偶配套，可以取代昂贵的铂铑热电偶。
CAS号：
性质：以难熔金属钼为基添加氧化物烧结成的材料。钼和钼合金与氧化锆、氧化铝等制取的金属陶瓷，具有熔点高、抗氧化性好、耐熔渣腐蚀、抗热震、抗磨等的优点。钼基金属陶瓷热电偶护管阳最高使用温度在还原与真空气氛中可这1700℃，与钨铼热电偶配套，可以取代昂贵的铂铑热电偶。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。