1) TiB2 based cermets
TiB2-Cu基金属陶瓷
1.
TiB2 based cermets with different copper content were produced from titanium powder, boron powder and copper powder by Self-propagating High-temperature Synthesis under conditions of Pseudo Hot Isostat-ic Pressing (SHS/PHIP).
利用自蔓延高温燃烧合成结合准热等静压技术制备了不同Cu含量的TiB2-Cu基金属陶瓷。
2) TiB_2 cermet
TiB2基金属陶瓷
1.
Experimental results show that the bending strength of TiB_2 cermet decreases and the Rockwell hardness increases with sintering temperature rising up; a bending strength peak appears with holding time prolonged.
以Fe Ni Ti Al为助烧剂,用热压的方法制备了TiB2基金属陶瓷。
3) NiFe_2O_4-Cu cermet
NiFe2O4-Cu金属陶瓷
4) Cu_2O-Cu cermet
Cu_2O-Cu金属陶瓷
1.
A new Cu_2O-Cu cermet material with different Cu shape and size was prepared as candidate inert anode material for Al production.
本文以铝电解用惰性阳极材料为主要应用背景,提出了新的Cu_2O-Cu金属陶瓷材料体系,设计和制备了含有不同形貌和尺寸Cu颗粒的Cu_2O-Cu金属陶瓷。
5) Cu/Cu_2O cermets
Cu/Cu_2O金属陶瓷
1.
The Cu/Cu_2O cermets prepared with hot pressing technology wereproduced by hot pressing the spherical and Cu_2O powders or branched Cu and Cu_2Opowders.
本文通过对Cu/Cu_2O金属陶瓷微观组织表征和导电性的测量,系统研究了导通相Cu含量、形貌、尺寸对金属陶瓷逾渗行为的影响规律,并在此基础上,分析了逾渗临界指数的非普适性,提出以骨架密度表征有效导通相含量,为在更深层次上认识导体/绝缘体材料的逾渗机理做出了一定的贡献。
6) Ti3C2/(Cu-Al) cermet
Ti3C2/(Cu-Al)金属陶瓷
1.
A sub-micro-layered Ti3C2/(Cu-Al) cermet was prepared by in-situ hot pressing a mixture of Ti3AlC2 and copper powders.
以Ti3AlC2和Cu粉作为原料,在1150℃下原位热压反应制备了具有亚微米层状结构的Ti3C2/(Cu-Al)金属陶瓷材料。
补充资料：钼基金属陶瓷
分子式：
CAS号：
性质：以难熔金属钼为基添加氧化物烧结成的材料。钼和钼合金与氧化锆、氧化铝等制取的金属陶瓷，具有熔点高、抗氧化性好、耐熔渣腐蚀、抗热震、抗磨等的优点。钼基金属陶瓷热电偶护管阳最高使用温度在还原与真空气氛中可这1700℃，与钨铼热电偶配套，可以取代昂贵的铂铑热电偶。
CAS号：
性质：以难熔金属钼为基添加氧化物烧结成的材料。钼和钼合金与氧化锆、氧化铝等制取的金属陶瓷，具有熔点高、抗氧化性好、耐熔渣腐蚀、抗热震、抗磨等的优点。钼基金属陶瓷热电偶护管阳最高使用温度在还原与真空气氛中可这1700℃，与钨铼热电偶配套，可以取代昂贵的铂铑热电偶。