1) Zn-Al HTALs
Zn-Al类水滑石
1.
46 mg P·g-1 in sludge filtrate of a sewage work by Zn-Al HTALs was obtained when the adsorbent was prepared at 70℃ using NaOH solution as the coprecipitant,aged for 6 h and calcined at 300℃ for 4 h.
采用共沉淀法制备了一系列Zn-Al类水滑石吸附剂,并考察了制备条件对其磷酸盐吸附性能的影响。
2) Zn-Mg-Al hydrotalcite-like materials(LDHs)
Zn-Mg-Al类水滑石
1.
Zn-Mg-Al hydrotalcite-like materials(LDHs) were synthesized by a coprecipition method and characterized by XRD,IR to prove its hydrotalcite-like structure.
采用共沉法制备Zn-Mg-Al类水滑石并且利用XRD,IR等手段对催化剂进行表征,研究Zn-Mg-Al类水滑石及其焙烧产物对酯交换反应的催化活性。
3) Zn/Al Hydrotalcite
Zn/Al水滑石
4) Zinc-Aluminium-hydrotalcite(Zn-Al-LDH)
Zn-Al型水滑石
1.
The authors have designed a dissolved CO2 microelectrode based on polydimethylsiloxane(PDMS) gel and Zinc-Aluminium-hydrotalcite(Zn-Al-LDH) ion carrier complex membrane,which can be used to detect deep-ocean CO2 abnormality.
本文设计的基于自制的聚二甲基硅氧烷胶与Zn-Al型水滑石复合膜为离子载体的溶解CO2探测电极属于电势型CO2电极,适用于对深海中溶解形式的CO2的测量,具有体积微小、便于与pH、盐度、温度、氧化还原电位等多种传感器集成在同一探头腔内,实施在线探测等优点。
5) Nano Zn/Al-LDH
纳米Zn/Al-水滑石
1.
Objective To explore and compare the oxidative damage induced by Nano Zn/Al-LDH.
目的探讨纳米Zn/Al-水滑石颗粒对Hela细胞的氧化作用。
6) Ni-Al hydrotalcite
Ni-Al类水滑石
1.
Ni-Al hydrotalcite was synthesized by a hydrothermal method utilizing urea hydrolysis with n(Ni2+):n(Al3+):n(urea)=2∶1∶10 and 3∶1∶10.
采用尿素分解水热合成Ni-Al类水滑石,其中使Ni2+/Al3+/尿素的摩尔比为2∶1∶10和3∶1∶10。
补充资料：Al-Zn east aluminium alloy
分子式：
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
CAS号：
性质：以锌为主要合金元素的铸造铝合金，是最早获得工业应用的铝合金之一。在工业中应用的Al-Zn系铸造铝合金成分是5％～14％Zn，2％～3％Cu，6％～8％ Si，0.1％～0.7％Mg，并含有少量其他元素。Al-Zn-Cu合金强度较高、切削加工性能和焊接性能良好，但铸造性能和抗腐蚀性能差。Al-Zn-Mg合金具有良好的力学性能和抗腐蚀性能，可以在淬火时效状态下使用，具有更高的强度。另外该合金的熔化温度较高，但其铸造工艺性能较差。Al-Zn-Si合金具有较高的力学性能和良好的铸造性能，广泛用于砂型、金属型和压力铸造。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条