1) modified rubber
改性橡胶
1.
One kind of modified rubber with good damping properties in the temperature range from 60 ℃ to 120 ℃ was prepared by blending polyvinyl chloride(PVC) resin paste and chlorobutyl rubber(CIIR) to improve the damping properties of CIIR in higher temperature region.
采用聚氯乙烯(PVC)糊树脂共混改性氯化丁基橡胶(CIIR)方法,制备了一种在60~120℃阻尼效果良好的改性橡胶材料,以解决氯化丁基橡胶阻尼温域较低的缺陷。
3) modified silicon rubber
改性硅橡胶
1.
The modified silicon rubbers, which have expected molecule structures demonstrated by IR spectra, were used to toughen epoxy resin.
用改性硅橡胶对环氧树脂进行增韧改性 ,通过对增韧体的冲击强度测试结果表明 ,在改性硅橡胶加入量为 0～ 15份的范围内 ,增韧体的冲击强度随着改性硅橡胶的加入量升高而明显增大 ,加入量超过 15份以后 ,增韧体的冲击强度增势缓慢 ,改性硅橡胶对环氧树脂具有良好的增韧效果。
5) waste rubber modified
废橡胶改性
1.
In this paper,the working Performance,mechanical properties and dynamic performance of waste rubber modified concrete has been studied.
本文主要研究了废橡胶改性混凝土的工作性能、力学性能和动力性能。
6) Crumb rubber modified asphalt
橡胶粉改性沥青
1.
It has important application value to get estimation methods for temperature susceptibility of crumb rubber modified asphalt by researching on it.
沥青路面的抗车辙能力、抗低温开裂能力和耐久性能等主要技术性质均与沥青的感温性有内在的联系,因此,通过对橡胶粉改性沥青的温度敏感性进行研究,得出适合于橡胶粉改性沥青温度敏感性的评价方法,具有重要的应用价值。
2.
The adoption of crumb rubber modified asphalt not only can improve the performance of asphalt at high or low temperature，reduce the asphalt pavement cracking and aging, improve the safety for vehicle drives and road service life, but also do not increase the cost, combining can make a contribution to the recovery of the discarded rubber and environmental protection .
采用橡胶粉改性沥青，不但可以改善沥青的高低温性能，减少沥青路面的龟裂和老化，提高车辆的行驶安全和道路使用寿命，而且不增加改性沥青的成本，并可为废旧橡胶的回收利用、保护环境做出贡献。
3.
With a view to studying sound absorption characteristics of porous crumb rubber modified asphalt pavement,standing-wave tube experiments are conducted at different frequencies on the porous rubber modified asphalt mixture with 20% porosity and ordinary asphalt mixture with 4% porosity.
为研究多孔橡胶粉改性沥青路面降噪吸声特性,利用驻波管分别对30 mm、40 mm、50 mm厚,孔隙率为20%的多孔橡胶粉改性沥青混合料试件和孔隙率为4%的普通沥青混合料试件进行了不同频率下吸声特性试验。
补充资料：橡胶模具、橡胶压模、橡胶硫化模
分子式：
CAS号：
性质：又称橡胶模具、橡胶压模、橡胶硫化模。用于压制橡胶产品的金属模型。一般用钢材(如45号钢)按图纸要求经机械加工而制得，并经热处理以提高其硬度及耐磨性。模具型腔与产品结构相同，型腔尺寸必须考虑不同橡胶的收缩率，在产品尺寸基础上进行放大或缩小，方可得到合适的产品尺寸。模具从工艺操作考虑还要设置流胶槽、启模口、定位销等。
CAS号：
性质：又称橡胶模具、橡胶压模、橡胶硫化模。用于压制橡胶产品的金属模型。一般用钢材(如45号钢)按图纸要求经机械加工而制得，并经热处理以提高其硬度及耐磨性。模具型腔与产品结构相同，型腔尺寸必须考虑不同橡胶的收缩率，在产品尺寸基础上进行放大或缩小，方可得到合适的产品尺寸。模具从工艺操作考虑还要设置流胶槽、启模口、定位销等。