1) direct rolling
直接轧制
1.
The direct rolling technology for conventional hot wide strip mill used in Europe and America;
欧美宽带钢常规流程直接轧制技术
2.
With the steelmaking-casting-direct rolling process in laboratory,the influence of different charging temperature on microstructure and properties of X70 pipeline steel were researched.
采用实验室炼钢—连铸—直接轧制方法,研究了用连铸连轧工艺生产X70管线钢时不同的热装温度对成品组织性能的影响,结果表明,800℃热装比1100℃热装的钢板晶粒尺寸细小,位错密度高,因而强度较高,韧性也能满足要求;而1100℃热装的钢板,析出物尺寸比800℃热装时细小、分散,韧性较好。
3.
The conventional hot rolling production technologies, including the endless rolling technology, the hot-delivery, hot charging and direct rolling of continuous cast billets, the ferrite - rolling technology, as well as the lubrication and automatic control techniques for hot rolling, are overviewed in this discussion.
介绍了传统热连轧新技术,包括无头轧制技术、连铸板坯热送热装和直接轧制技术、铁素体轧制技术、热轧工艺润滑技术、自动化控制技术的特点。
2) hot direct rolling
直接热轧制
3) CC DR
连铸-直接轧制
4) CC-DHCR
直接热装轧制
5) HDR(hot direct rolling)
[冶]热坯直接轧制
6) HCC(horizontal continuous casting)
[冶]热装直接轧制
补充资料：直接轧制
直接轧制
direct rolling
zh一J le Zhozh-直接轧制(direet rolling)由初轧厂生产的高温钢坯直接进入成品轧机轧成成品。其主要优点是:利用钢坯余热，节能;减少金属氧化，提高成材率。在直接轧制中，钢坯没有冷态下的表面检查(见钢坯检查)和清理(见钢坯表面清理)工序，必须在热态下进行火焰(见钢坯火焰清理)或人工清理，消除钢坯的表面缺陷，或者采用无缺陷钢锭，尽量减少钢坯表面的缺陷。经剪断后的合格高温钢坏直接送入成品轧机，为了保证成品轧机的终轧温度，应尽可能提高钢坯温度及初轧机的开轧温度。初轧板坯送入热带钢轧机直接生产带钢已在生产中运用。某些大断面的型钢也可用直接轧制法生产。如何进一步扩大直接轧制的规格品种范围，平衡初轧机与成品轧机的生产，是今后研究的课题。小断面的钢坯，由于温降大，进入成品轧机直接轧制前需要进行在线补充加热，以保证轧件的终轧温度。 (唐伟林)