1) temperature of burnt zone
烧成带温度
2) sintering temperature
烧成温度
1.
Effect of sintering temperature on performance of low-heat Portland cement and its mechanism;
烧成温度对低热水泥性能的影响及其机理研究
2.
By means of DTA and XRD, the influence of sintering temperature on the formation and properties of C2.
利用DTA和XRD方法,研究了烧成温度对硫铁铝酸钡钙矿物性能的影响。
3.
The microstructure and the room-temperature resistivity of BaTiO3-based PTC in different sintering temperature(1280℃,1300℃,1320℃) was observed by SEM.
实验以常用电子陶瓷工艺制备BaTiO3基PTC材料时,通过观察不同烧成温度(分别为1280℃,1300℃,1320℃)的PTC材料的阻温曲线并且通过扫描电镜(SEM)观察其显微结构,发现烧成温度越高,晶粒发育的越好,并且烧成温度升高,材料出现过烧现象,材料的玻璃相和气孔率增大,从而室温电阻率增大。
3) firing temperature
烧成温度
1.
The relationship of the porous ceramics properties with firing temperature and the main materials particle size is also discussed.
本研究以石英和长石为主要原料 ,通过控制石英和长石的粒度和配比 ,研制出一种高强度的微米级多孔陶瓷 ,并讨论了骨料粒径和烧成温度与其性能之间的关系。
2.
The influence of firing temperature on the structure and electrical properties of tin oxide conductive ceramic were researched by using X ray Diffraction and measuring electrical properties.
本文通过 X-射线衍射分析及阻温特性测定等方法研究了 Sn O2 导电陶瓷的晶相组成和电性能与烧成温度的关系。
3.
The firing temperature varied in a.
陶器的烧成温度从新石器时代的７５０～８００℃，延续至春秋战国时期的１０５０～１１５０℃，到东汉的１１５０～１２００℃。
4) low firing temperature
低烧成温度
5) Sintering Temperature range
烧成温度范围
1.
The result shows that the ball sintering temperature decreases,while sintering temperature range enlarges with the pressure increase;the highest density and the lowest wear rate is obtained at the pressure of 100MPa.
结果表明:在本研究系统内随着压力的增加,瓷球的烧结温度下降,烧成温度范围拓宽。