1) calcination temperature
煅烧温度
1.
Effect of calcination temperature on the structure and catalytic properties of perovskite mixed-oxide for simultaneous removal of NO_x and soot;
煅烧温度对钙钛矿复合金属氧化物的结构及其同时催化去除NO_x和碳烟的影响
2.
Suitable calcination temperature of activate kaolin clay;
活化高岭土适宜煅烧温度
3.
Effects of calcination temperature on structure of titanium oxide photocatalyst
煅烧温度对二氧化钛光催化剂结构的影响
2) calcining temperature
煅烧温度
1.
The best PH range was investigated,and the effects of calcining temperature and holding time on the size of nanometer-sized particles were also studied.
探讨了共沉淀法制备SnO2 CuO的最佳PH值范围 ,研究了煅烧温度和保温时间对纳米粒子尺寸的影响。
2.
The morphology of the particles was observed by means of scanning electron microscopy and the influence of calcining temperature to particle's morphology was studied.
借助热分析仪(DSC)分析了共沉淀产物的热分解过程,确定了共沉淀产物的煅烧温度范围,采用三个不同煅烧温度煅烧得到BaTiO3粉体。
3.
Results show that with the increase of calcining temperature,the grain becomes larger and d(111)and an axis becomes shorter while c axis becomes longer gradually.
通过DSC对其进行热分析,确定两个煅烧温度:780℃和900℃。
3) burning temperature
煅烧温度
1.
The effect of flour-sulfur contained quarry A formed under different burning temperature on cement hydration;
不同煅烧温度下形成的含氟硫A矿对水泥水化性能的影响
2.
Study on optimum burning temperature of white cement by soda residue;
碱渣烧制白色水泥适宜煅烧温度的研究
3.
Using burnability index to control the burning temperature of rotary kiln;
用生料易烧性指数控制回转窑煅烧温度
4) calcined temperature
煅烧温度
1.
The results show that when the calcined temperature increases,the grain size increases and the absorption profile shifts to longer wave to some degree.
以钛酸四正丁酯为原料,采用溶胶-凝胶法制备了不同煅烧温度(500℃、600℃、700℃和800℃)的TiO2纳米粒子,对样品进行了TG-DTA、XRD、UV-Vis及IR分析,并以甲基橙为目标降解物,考察了煅烧温度对TiO2光催化性能的影响。
2.
The effects of calcined temperature on the characteristics of SrTiO3 Powder prepared by chemical coprecipitation method were studied by TG-DTA, XRD, SEM, etc.
通过研究不同煅烧温度对粉料性能的影响,认为粉料前驱体在800～900℃煅烧1小时后所得SrTiO_3粉料烧结活性较好。
5) calcinations temperature
煅烧温度
1.
The property of the granular bentonite was measured,the influences of calcinations temperature and absorbed time on adsorption property were discussed.
测试了样品的性能,讨论了煅烧温度、吸附时间对吸附性能的影响。
2.
It analyzes origin of activity of coal gangue and method on acting it,and also analyzes influencing factors to its forming from calcinations temperature、calcinations time、cooling means、maintenance condition and fineness,then puts forward some suggestion combined with research finding in domestic.
对煤矸石活性来源及激活煤矸石活性的方法进行了分析;从煅烧温度、煅烧时间、冷却条件、养护条件及细度等方面分析了煤矸石活性形成的各种影响因素,并结合国内的研究成果,提出了一些建议。
3.
The calcinations temperature and ageing time influence the performance of desulphurization gypsum.
脱硫石膏的煅烧温度和陈化时间会对石膏浆体的性能产生影响,特别要注意陈化时间过长时,脱硫石膏会吸收过多的水分,出现不凝结的现象。
6) temperature gradient calcination
温度梯度煅烧
补充资料：铂电阻温度表(见电阻温度表)
铂电阻温度表(见电阻温度表)
表。bod旧nZu wendubiao铂电阻温度表见电阻温
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条