1) ratio loading and unloading path
关键词比例加载和比例卸载
2) Proportional loading
比例加载
1.
Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
2.
Biaxial fatigue behaviors of the Zr-4 alloy under proportional and non-proportional loading with the phase angles of 30°, 60° and 90° were studied.
研究了冷变形Zr-4合金在双轴比例和非比例加载下的循环变形行为,结果表明:当循环应变幅较低时,Zr-4合金表现为循环初始硬化随后饱和的特征;随着应变幅提高,初期硬化后,表现为连续循环软化特征;高应变幅下,初期硬化消失,表现为急剧的循环软化。
3.
The deformation behavior of hydrided zircaloy-4 under tension-torsion proportional loading was investigated using the quantitative metallography and the finite element method(FEM).
采用有限元数值分析方法,模拟了含氢化物Zr-4合金拉-扭双轴比例加载下的变形行为。
3) Proportional and nonproportional loading
比例加载与非比例加载
4) non-proportional loading
非比例加载
1.
Fatigue fracture characteristics of GH4169 super-alloy under non-proportional loading at high temperature;
GH4169合金高温多轴非比例加载下疲劳断口特征
2.
Investigation of fatigue damage parameters under multi-axial non-proportional loading;
多轴非比例加载条件下疲劳损伤参量的研究
3.
Multiaxial fatigue behavior of superalloy GH4169 was investigated by using the thin tubular multiaxial fatigue specimens under proportional and non-proportional loadings at high temperature.
高温多轴疲劳试验采用比例与非比例加载路径。
5) nonproportional loading
非比例加载
1.
Low cycle fatigue properties of cast aluminum alloys 356 under multi-axial nonproportional loading have been investigated in this paper.
结果表明,合金在循环变形过程中表现为循环硬化特征,循环硬化的程度表现出对非比例加载路径的依赖性;在相同等效应变幅值下,合金的非比例加载低周疲劳寿命小于比例加载,且非比例加载低周疲劳寿命也表现出对非比例加载路径的依赖性;在多轴疲劳寿命预测模型中考虑非比例加载路径对疲劳寿命的影响可以大大提高寿命模型预测的精确度。
2.
Based on the micromechanism of multiaxial low cycle fatigue under nonproportional loading of 316L stainless steel,maxium shear strain and nonproportionality of strain paths are considered as damage parameters of low cycle fatigue.
利用对 316L不锈钢多轴非比例加载低周疲劳的试验结果 ,对现有的多轴低周疲劳寿命估算方法进行了讨论 ,基于 316L不锈钢非比例加载低周疲劳的微观机理 ,选择最大剪应变以及应变路径的非比例度作为损伤参量 ,建立了基于临界面方法的新的非比例加载低周疲劳寿命估算公式 ,利用新的非比例加载低周疲劳寿命估算公式对寿命的预测结果表明 :新的寿命估算公式对剪切型破坏的 316L与 316LN不锈钢及拉伸型破坏的 30 4不锈钢非比例加载低周疲劳寿命预言能力比现有的临界面方法精确 。
3.
The case of nonproportional loading and the plastic dissipation of neartip field is discussed in this paper.
本文采用拟全量理论，分析了裂尖区的非比例加载情况，并从理论上导出不同屈服程度下塑性能密度Ｗ，场的统一表达式，有限元场分析证实了此表达式的正确性。
6) out-of-phase loading
非比例加载
1.
Macroscopic response and microscopic substructure have been studied for the cold-worked and stress-released Zr-4 alloy under biaxial out-of-phase loading with phase angles of 30°, 60°, 90° and equivalent strain amplitudes of 0.
4％时双轴非比例加载下,冷变形去应力状态Zr-4合金的宏观响应和微观位错亚结构。
2.
Fatigue experiments of LY12CZ allumimum alloy thin-walled tubularspecimens are conducted under axial tension-compression,pure torsion and 90°out-of-phase loading.
针对非比例加载路径对金属材料的疲劳行为及疲劳寿命的影响进行了研究。
补充资料：比例税率
税基与税额成等比例变化，不以税基大小为转移的税率。税率的一种类型。
比例税率有多种类型。按自身的表现形式划分，有以绝对额形式表示的额式比例税率和以百分比形式表示的率式比例税率。按对征税对象或纳税人的使用方式划分，有统一比例税率和差别比例税率。统一比例税率是对不同的征税对象和纳税人，均按统一的比率计算应纳税额;差别比例税率是对不同的征税对象和纳税人,分别按不同的比例计算应纳税额，如产品差别比例税率、行业差别比例税率、地区差别比例税率等。
比例税率的共同特点是税额与税基始终保持同一比率,税额随税基的增减而同比率增减。从财政方面看,它可使税收收入随经济的变化而变化,具有一定的弹性,在经济不断发展的情况下，税收收入也会不断增加。从经济方面看，它可使税收负担随收入的变化而变化，收入多者负担多，收入少者负担少。但在贯彻社会政策方面，由于收入多者和收入少者的负担能力不尽相同，按照同一比率征税，存在表面平等掩盖实际不平等的弊病。因此在实际运用中,比例税率主要适用于对商品的课税,而对所得或财产的课税则大多使用累进税率。
比例税率有多种类型。按自身的表现形式划分，有以绝对额形式表示的额式比例税率和以百分比形式表示的率式比例税率。按对征税对象或纳税人的使用方式划分，有统一比例税率和差别比例税率。统一比例税率是对不同的征税对象和纳税人，均按统一的比率计算应纳税额;差别比例税率是对不同的征税对象和纳税人,分别按不同的比例计算应纳税额，如产品差别比例税率、行业差别比例税率、地区差别比例税率等。
比例税率的共同特点是税额与税基始终保持同一比率,税额随税基的增减而同比率增减。从财政方面看,它可使税收收入随经济的变化而变化,具有一定的弹性,在经济不断发展的情况下，税收收入也会不断增加。从经济方面看，它可使税收负担随收入的变化而变化，收入多者负担多，收入少者负担少。但在贯彻社会政策方面，由于收入多者和收入少者的负担能力不尽相同，按照同一比率征税，存在表面平等掩盖实际不平等的弊病。因此在实际运用中,比例税率主要适用于对商品的课税,而对所得或财产的课税则大多使用累进税率。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条