1) cold pressure welding
冷压焊
1.
Research on Al-Cu heterogeneous metal cold pressure welding and its joint microstructure and performances;
铝铜异种金属冷压焊及其焊缝接头显微组织和性能
2.
Although these hypotheses can explain some phenomena of cold pressure welding ,many defects exist.
在近年来 ,国内外关于冷压焊的结合机理出现了不少假说 ,虽然这些理论解释了冷压焊中的一些现象 ,但存在着许多缺陷和不足 。
2) cold press welder
冷压焊机
3) Vacuum Cold Welded
真空冷压焊
4) cold welding technology under explosive pressure
爆压冷焊技术
1.
This article introduces the design principle,design planning,welding effect and technology characteristic of cold welding technology under explosive pressure for rail.
介绍了利用爆压冷焊技术研制开发的一种新型的“爆压冷焊式钢轨接续线技术”的设计原则、设计方案、焊接效果及技术性能。
5) cold welding
冷焊
1.
Application of “cold welding” technique in restoring slurry pump;
“冷焊”技术在修复渣浆泵中的应用
2.
Application of cold welding in repairing crack of cylinder body;
冷焊工艺在汽缸体裂纹修理上的应用
3.
Ultrasonic inspection to detect cold welding in electro-fusion joint of polyethylene pipes;
聚乙烯电熔接头冷焊缺陷的超声检测方法
6) cold-welding
冷焊
1.
Study on the carbides in cold-welding surfacing metals;
冷焊焊缝中的碳化物研究
2.
This paper presents an overview of cold-welding steel roll to eliminate local defeCts.
全面介绍了钢轧辊局部缺陷修复的实用冷焊工艺。
补充资料：冷压焊
在常温下只靠外加压力使金属产生强烈塑性变形而形成接头的焊接方法。加压变形时，工件接触面的氧化膜被破坏并被挤出，能净化焊接接头。所加压力一般要高于材料的屈服强度，以产生60～90％的变形量。加压方式可以缓慢挤压、滚压或加冲击力，也可以分几次加压达到所需的变形量。冷压焊的工件一般是塑性金属,如铝、铜、镉、镍和银等。冷压焊有搭接点焊和对接焊两种。搭接点焊前工件表面须经机械加工,或用钢丝刷(轮)或溶剂仔细清理，对接焊时表面清理要求不太严格。冷压焊设备只需一台挤压机，包括压膜和夹持钳口，也可用手动夹具焊接小工件。冷压焊时工件不必加热，因而适于焊接不允许有温升的工件和加热时会引起软化的材料，也适用于易产生脆性化合物的异种金属连接。冷压焊已应用于电容器外壳的封装、电气工业中铝铜过渡接头、导电母线、引出线、铝制日用品和包装带的焊接等。铝与铝对接可焊截面达1500毫米2,铝与铜对接可焊截面达1000毫米2。冷压焊所需设备简单，工艺简便,劳动条件好。但冷压焊所需挤压力较大，在大截面工件的焊接时设备较庞大，搭接焊后工件表面有较深的压坑，因而在一定程度上限制了它的应用范围。