1) layer free of eta-phase
无η相层
1.
It were found that perfect gradient structure can be gained by single sintering,and the thickness of layer free of eta-phase increase with the increase of carburizing tem- perature and holding time,and the efficiency of carburization of single sintering is higher than that of two step sinter.
结果表明:如工艺控制得当,一次烧结法可以制备出较理想的梯度结构,随着渗碳温度和保温时间的增加,无η相层厚度增大,一次烧结法比二次烧结法的渗碳效率更高。
2) η phase
η相
1.
The results show that,in carbon-deficient cemented carbides,carbon content affects the type,amount and distribution of η phase,WC shape and properties of alloys.
结果表明:碳含量影响合金中η相的类型、含量、分布、WC的形状以及合金的性能;Co3W3C相出现在缺碳程度相对较小的合金中,其含量随碳含量的增加而增大,而Co6W6C相与之相反;合金中的η相总量随碳含量的增大而减少;随着缺碳程度的增加,合金中η相的分散均匀性变差,并且η相趋向于成大块状;WC大多呈现多角特征;合金的密度和维氏硬度随着碳含量的增加,先大幅度增加后缓慢减小,碳含量为5。
2.
The results showed that the cemented carbide predecessor matrix with different carbon deficient all gets homogeneous microstructure with WC+Co+η phases;and the content of η pha.
采用贫碳配料的方法制备了η相均匀弥散分布的梯度硬质合金渗碳前驱基体,通过对渗碳基体显微组织的观察,研究了贫碳量对渗碳基体显微组织的影响。
3.
The results show that there are the most η phase using the filling alloy with Fe and there are the lest η phase using the filling alloy with Ni-Fe.
结果表明,纯Fe作为填充金属时,界面处产生的大块η相最多,Co-Fe合金次之,Ni-Fe合金最少。
3) η-phase
η-相
4) precipitatesη,η'
η',η析出相
1.
Analysis of structural models of precipitatesη,η′in Al-Zn-Mg alloys;
Al-Zn-Mg合金中η′,η析出相结构模型的分析
5) morphology of η
η相形态
6) secondary η phase
次生η相
1.
The precipitation mechanism of secondary η phase in a FeNi-based alloy;
Fe-Ni基合金中次生η相的析出机理
补充资料：(η6-benzene)( η5-2,4-cyclopentadien-1-yl)manganese
分子式：
CAS号：
性质：深红色结晶。一种异环夹心结构。三羰基合锰中的三个羰基被苯取代后制得。用作化学试剂。
CAS号：
性质：深红色结晶。一种异环夹心结构。三羰基合锰中的三个羰基被苯取代后制得。用作化学试剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条