1) slip band
滑移带
1.
Preparation of metallic samples with slip band during cold plastic deformation and experimental performance
金属冷塑性变形滑移带样品制备及实验运行
2.
The mopohology of slip bands for materials with two different slip modes: pure Cu and Cu-Zn alloy after prestraining and cyclic softening has been observed.
Ｃｕ－Ｚｎ合金循环软化后有两种衬度的滑移带，而纯Ｃｕ则主要表现为驻留滑移带，说明两种材料疲劳应变的容纳方式不同。
3.
On the basis of full consideration of the slip band appearing and the shape fixability of forming parts,reasonable conditions in stretch forming of airplane mirror skins have been determined by means of analysis of the effects of stretching velocity, geometrical dimensions of blank, geometrical parameters of dies and lubrication methods on forming quality.
在充分考虑滑移带出现与成形件贴模度的基础上，通过分析拉形速度、毛料几何尺寸、模具几何参数、润滑方式对成形质量的影响，确定了合理的飞机镜面蒙皮拉形条件。
2) gliding plane(zone)
滑移面(带)
3) slip band
滑移带<冶>
4) belt creep
皮带滑移
5) lüders line
滑移带群
6) track drift
履带滑移
补充资料：滑移带
滑移带
slip band
滑移带slip band晶体的塑性形变是通过沿一定晶体学平面，即滑移面的滑移产生的。塑性形变的结使原来光滑的试样表面变成台阶状。纯铝单晶塑性形后的表面形貌见图1。照片上的线条即是滑移带。它是滑移面沿着滑移方向滑移在试样表面留下的台阶的迹。用电子显微镜仔细观察这些条痕，发现每一条痕由许多密集的称为滑移线的平行线群所组成(图2)。‘蛛彝毅李燕羚诊郊图1铝单晶中的滑移带滑移带滑移量(台阶》原子间距 图2滑移带的示意图一条滑移线所对应的台阶高度叫滑移量，约为1000· 原子间距，它是上千个位错沿同一滑移面滑』 晶体的结果。滑移线之间的晶片称为滑移层 层厚约工00个原子间距。由滑移线组成的滑乡 带的宽度约与台阶高度相近，滑移带之间的l 离约10000个原子间距。晶体的滑移是不均， 分布的，滑移集中在某些晶面上，滑移带之l 的区域未发生滑移。(王中光)