1) persistent slip band (PSB)
驻留滑移带
1.
In single-slip-oriented copper single crystals which were cyclically deformed under constant plastic shear strain amplitude control, the persistent slip line (PSL) was first formed in the vein dislocation structure of matrix, and then it was rather quickly transformed into persistent slip band (PSB) under consecutive cycling.
在循环加载条件下,单滑移取向的Cu单晶体首先出现驻留滑移线(PSL),然后随着循环周次的增加转变为驻留滑移带(PSB),在不同温度、不同时间条件下对疲劳Cu单晶进行真空退火处理,观察PSB结构在热激活条件下的变化情况,结果表明,退火处理过程中由于空位浓度差异所产生的渗透力促使位错运动,并使PSB的某些部位逐步细化,以至消失,实现了PSB的分段相消,在退火过程中由于应变能的逐步释放,未观察到再结晶现象。
2) persistent slip bands (PSBs)
驻留滑移带
1.
The interactions of persistent slip bands (PSBs) with grain boundaries (GBs) and twin boundaries (TBs) were investigated.
对含有退火孪晶的多晶铜进行了不同塑性应变幅下的应变疲劳实验,利用扫描电镜及其电子通道衬度技术(SEM-ECC)观察了表面滑移形貌、疲劳裂纹和位错组态,研究了驻留滑移带与晶界和孪晶界的交互作用。
3) persistent slip band
驻留滑移带PSBs
4) evolution of persistent slip band
驻留滑移带的演化
5) persistent slip line (PSL)
驻留滑移线
1.
In single-slip-oriented copper single crystals which were cyclically deformed under constant plastic shear strain amplitude control, the persistent slip line (PSL) was first formed in the vein dislocation structure of matrix, and then it was rather quickly transformed into persistent slip band (PSB) under consecutive cycling.
在循环加载条件下,单滑移取向的Cu单晶体首先出现驻留滑移线(PSL),然后随着循环周次的增加转变为驻留滑移带(PSB),在不同温度、不同时间条件下对疲劳Cu单晶进行真空退火处理,观察PSB结构在热激活条件下的变化情况,结果表明,退火处理过程中由于空位浓度差异所产生的渗透力促使位错运动,并使PSB的某些部位逐步细化,以至消失,实现了PSB的分段相消,在退火过程中由于应变能的逐步释放,未观察到再结晶现象。
6) TR Tape Residence
磁带驻留
补充资料：滑移带
滑移带
slip band
滑移带slip band晶体的塑性形变是通过沿一定晶体学平面，即滑移面的滑移产生的。塑性形变的结使原来光滑的试样表面变成台阶状。纯铝单晶塑性形后的表面形貌见图1。照片上的线条即是滑移带。它是滑移面沿着滑移方向滑移在试样表面留下的台阶的迹。用电子显微镜仔细观察这些条痕，发现每一条痕由许多密集的称为滑移线的平行线群所组成(图2)。‘蛛彝毅李燕羚诊郊图1铝单晶中的滑移带滑移带滑移量(台阶》原子间距 图2滑移带的示意图一条滑移线所对应的台阶高度叫滑移量，约为1000· 原子间距，它是上千个位错沿同一滑移面滑』 晶体的结果。滑移线之间的晶片称为滑移层 层厚约工00个原子间距。由滑移线组成的滑乡 带的宽度约与台阶高度相近，滑移带之间的l 离约10000个原子间距。晶体的滑移是不均， 分布的，滑移集中在某些晶面上，滑移带之l 的区域未发生滑移。(王中光)