1) high molecular weight poly(vinyl chloride)
高分子量聚氯乙烯树脂
1.
The Brabander torque-rheometer with proprammable elevating temperature was used to study and compare the melting processes of two high molecular weight poly(vinyl chloride) resins(each having same molecular weight) and their plasticized systems in same shear stress.
采用程序升温Ｂｒａｂａｎｄｅｒ转矩－流变仪研究、比较了两种高分子量聚氯乙烯树脂（分子量相同）及其增塑体系在相同剪切应力作用下的熔融过程。
2) ultra high molecular weight PVC(UHMWPVC)
超高分子量聚氯乙烯树脂
3) ultra high molecular weight PVC resin
超高分子量聚氯乙烯树脂(UHMWPVC)
4) HMWPVC
高分子量聚氯乙烯
1.
DEVELOPMENT OF HMWPVC SEALING STRIP;
高分子量聚氯乙烯密封条的研制
2.
Study On the Properties of HMWPVC Blend Systems;
高分子量聚氯乙烯共混体系的性能研究
6) high chlorinated polyethylene resin
高氯化聚乙烯树脂
1.
One-pack epoxy-acrylate resin modified high chlorinated polyethylene anti-corrosive paint is prepared with high chlorinated polyethylene resin and epoxy-acrylate resin as the main binder,and anti-corrosive pigments.
以高氯化聚乙烯树脂和环氧丙烯酸树脂为主要成膜物质,添加防腐颜填料,制得单组分、附着力好、防腐性和耐候性优异的环氧丙烯酸树脂改性高氯化聚乙烯防腐涂料。
补充资料：超高分子量聚氯乙烯
分子式：
CAS号：
性质：又称超高分子量聚氯乙烯。指平均聚合度1700以上，工业产品2000～4500，有时可高达8000的一类聚氯乙烯树脂。由于分子量高，大分子链间缠结点增多，类似交联效应，因而塑性变形降低，回弹性增加，耐热、耐寒、耐疲劳、机械强度都有提高，使用温度范围宽。可采用悬浮法，本体法，乳液法或微悬浮法等工艺，在较低温度及链增长剂存在下，以高活性引发剂使氯乙烯聚合而制得。加入增塑剂后用于制备PVC热塑性弹性体，替代橡胶用作汽车内饰件，门窗密封条，耐热电缆护套，耐热软管及鞋底等。
CAS号：
性质：又称超高分子量聚氯乙烯。指平均聚合度1700以上，工业产品2000～4500，有时可高达8000的一类聚氯乙烯树脂。由于分子量高，大分子链间缠结点增多，类似交联效应，因而塑性变形降低，回弹性增加，耐热、耐寒、耐疲劳、机械强度都有提高，使用温度范围宽。可采用悬浮法，本体法，乳液法或微悬浮法等工艺，在较低温度及链增长剂存在下，以高活性引发剂使氯乙烯聚合而制得。加入增塑剂后用于制备PVC热塑性弹性体，替代橡胶用作汽车内饰件，门窗密封条，耐热电缆护套，耐热软管及鞋底等。