1) polyvinyl chloride-ferric chloride resin
聚氯乙烯三氯化铁树脂
1.
The preparation method and application as catalyst in the esterification, ester exchange reaction, acetalation (ketalation) and molecular rearrangement reaction of polyvinyl chloride-ferric chloride resin was introduction.
介绍了聚氯乙烯三氯化铁树脂的制备方法和作为催化剂在酯化作用、酯交换作用、缩醛(酮)化作用及分子重排等方面的应用,说明了反应历程。
2) chlorinated polyvinyl chloride-ferric chloride
氯化聚氯乙烯三氯化铁
4) poly(vinyl chloride) supported ferric chloride
聚氯乙烯支载三氯化铁
1.
A variety of aldehydes can be converted into acylals rapidly and conveniently in the presence of catalytic amounts of poly(vinyl chloride) supported ferric chloride reagent (PVC FeCl 3) at room temperature in excellent yields.
聚氯乙烯支载三氯化铁 (PVC FeCl3)试剂在室温条件下能方便快速催化各类醛与乙酸酐反应 ,以良好产率 (75 %～96% )生成相应乙酰缩
5) daiflon
['daiflɔn]
聚三氟氯乙烯树脂
6) high chlorinated polyethylene resin
高氯化聚乙烯树脂
1.
One-pack epoxy-acrylate resin modified high chlorinated polyethylene anti-corrosive paint is prepared with high chlorinated polyethylene resin and epoxy-acrylate resin as the main binder,and anti-corrosive pigments.
以高氯化聚乙烯树脂和环氧丙烯酸树脂为主要成膜物质,添加防腐颜填料,制得单组分、附着力好、防腐性和耐候性优异的环氧丙烯酸树脂改性高氯化聚乙烯防腐涂料。
补充资料：聚氯乙烯/氯化聚乙烯共混物
分子式：
CAS号：
性质：系以聚氯乙烯为主，以氯化聚乙烯作冲击改性剂或内增塑剂，配以其他助剂混合而成的多相共混物，所用氯化聚乙烯氯含量为30％～40％，添加量为5％～15％，具有良好的冲击韧性、耐候性及其他综合性能；也存在增塑聚氯乙烯中加入氯含量40％～48％的氯化聚乙烯作永久型增塑剂，改善低温脆性及耐久性。两者均可以机械共混制取，用于各种管材、型材、电线电缆、防水卷材及汽车内饰件等方面。
CAS号：
性质：系以聚氯乙烯为主，以氯化聚乙烯作冲击改性剂或内增塑剂，配以其他助剂混合而成的多相共混物，所用氯化聚乙烯氯含量为30％～40％，添加量为5％～15％，具有良好的冲击韧性、耐候性及其他综合性能；也存在增塑聚氯乙烯中加入氯含量40％～48％的氯化聚乙烯作永久型增塑剂，改善低温脆性及耐久性。两者均可以机械共混制取，用于各种管材、型材、电线电缆、防水卷材及汽车内饰件等方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。