1) Warm-rolling
温轧预变形
2) pre-heating deformation
预温变形
3) Pre-strain temperature
预变形温度
4) pre-finishing temperature
预精轧温度
1.
Few network carbides and fine laminar pearlite were obtained in the industrial experiment on increasing the pre-finishing temperature of GCr15 bearing steel 10 mm wire,and heat simulation method was used in laboratory to analyze industrial experiment phenomena.
通过提高GCr15轴承钢10 mm线材预精轧温度的工业试验,得到了网状碳化物少的细片状珠光体组织,利用实验室热模拟的方法对工业试验现象做了进一步分析。
5) cold rolling
冷轧变形
1.
The effect of cold rolling deformation prior to aging on the strengthening of a maraging steel was investigated.
系统研究了预先冷轧变形对马氏体时效钢强化的影响,研究结果表明:510℃×3 h时效引起的强度净增加值恒定,与冷轧变形量无关,最终的强度为:σ=σ0+ΔσCR+ΔσAge,即初始强度、冷加工强化和时效强化的叠加,其中只有冷加工强化ΔσCR随变形量变化。
2.
The article introduces microstructure evolution and mechanical hardening of three different kind steels during cold rolling.
本文介绍了三种钢在冷轧变形过程中的组织演变和形变强化规律，发现三种钢具有不同的形变强化规律。
6) rolling deformation
轧制变形
1.
The influence of rolling deformation and heat treatment temperature on structures, mechanical properties is studied.
X射线衍射结果表明,随着轧制变形量的增加,Ti50Ni47Fe3合金在轧制方向上出现了择优取向;Ti50Ni47Fe3合金的晶粒尺寸随着轧制变形量的增加而减小,随着热处理温度的升高而增大;Ti50Ni47Fe3合金的抗拉强度和屈服强度随着轧制变形量的增加而增大,随热处理温度的升高而降低。
2.
The results show that the orientation distribution calculated by the FC (full constraints)Taylor model is closer to experimental results than those by other models at the low rolling deformation de.
结果表明:在低轧制变形程度时,完全限制(FC)模型计算结果的取向分布较其它模型更符合实际结果。
3.
The results show that the rolling textures for the sample with initial randomly distributed texture mainly consists of C,S and B components during rolling deformation while the orientation density values for the three textures only have slight difference, most crystallites a.
结果表明:随着轧制变形的进行,对于初始自由分布的样品,晶粒取向主要向α,β取向线附近聚集,其形变织构主要由C,S及B织构组成,且3种织构成分密度值相差不大;对于初始具有近似立方织构的样品,晶粒取向主要向β取向线上聚集,其形变织构主要由C,S织构组成,B织构成分相对较弱。
补充资料：温轧
温轧
warm rolling
WenZhQ沮轧(warm rolling)在金属或合金常温组织发生回复的温度以上，再结晶的温度以下的温度范围内进行的乳制过程。由于温轧时材料的加工硬化得到一定的回复，与冷轧相比，材料的屈服强度低，塑性高，又没有热轧的缺点，因此受到普遍重视。温轧一般在冷轧设备上进行。在进入轧制变形区之前用感应加热器将工件加热到200一400‘C，然后进行轧制。一些塑性低、强度高的金属通过温轧也有可能得到精加工。温轧的延伸率约为冷轧的2一3倍。 温轧适用于加工一些在常温条件下塑性低、屈服强度高、变形抗力大、不适合采用冷轧的金属和合金。也用来加工那些虽能冷轧，但生产效率低、轧程多、能耗大的金属和合金，如轧制铁铝合金、不锈钢板等。 (韦光)