1) thermal fatigue failure
![点击朗读](/dictall/images/read.gif)
热疲劳失效
1.
Based on the study on types and reasons for thermal fatigue failure of hot-extrusion dies made form 5Cr4W5Mo2V steel,the ways and methods of improing resistance to thermal fatigue of the dies have been involved.
通过5Cr4W5Mo2V热挤压凸模热疲劳失效形式及原因的研究,探讨了提高模具热疲劳性能的途径与方法。
2) fatigue invalidation
![点击朗读](/dictall/images/read.gif)
疲劳失效
1.
In view of the fatigue invalidation of submarine pipeline span caused by vortex-induced vibration, the reliability analysis method of nonlinear vortex-induced vibration invalidation of pipe]the span is proposed.
针对由涡激振动引发的海底管跨疲劳失效,提出管跨非线性涡激振动失效可靠性分析方法,引入波浪和海流对管跨的联合作用以及管跨所受轴力,并考虑管跨海底土壤支撑端的实际工况,建立了管跨段的垂向非线性振动方程及其边界条件,通过模态分析,求得振动方程的固有振型,并以此为基础,推导和建立方程解的关于时间域的微分方程组,运用时频分析方法,由波浪谱推得的波、流力谱作为振动方程的输入谱,计算得到相应的输出谱,进而确定位移和应变等各种响应随机过程的概率分布,结合可靠性理论确定管跨的疲劳失效概率,最后,通过实例的计算与分析,确定几个重要参数对管跨疲劳失效的影响程度。
2.
The vortex induced vibration of pipeline span is the leading factor of fatigue invalidation of pipeline, and is the most important confronted and urgent to be solved problem during the reliability design and evaluation of pipeline span.
管跨的涡激振动是引发管跨发生疲劳失效的主要因素之一 ,也是管跨可靠性设计、可靠性评估工作所要解决的主要问题。
3) Fatigue Failure
![点击朗读](/dictall/images/read.gif)
疲劳失效
1.
Dynamic reliability analysis of offshore platform considering fatigue failure;
![点击朗读](/dictall/images/read.gif)
考虑疲劳失效的海洋平台动态可靠性分析
2.
Fatigue Failure Analysis of Rolling Bearings;
![点击朗读](/dictall/images/read.gif)
滚动轴承疲劳失效过程的分析与研究
3.
Microscopic mechanism of XCQ16 and 20Mn2 axle steel fatigue failure
![点击朗读](/dictall/images/read.gif)
XCQ16和20Mn2车轴用钢疲劳失效的微观机理
4) static fatigue failure
![点击朗读](/dictall/images/read.gif)
静疲劳失效
5) Fatigne failure life
![点击朗读](/dictall/images/read.gif)
疲劳失效寿命
6) fatigue failure probability
![点击朗读](/dictall/images/read.gif)
疲劳失效概率
1.
This paper analyses and calculates the fatigue failure probability of the tubularwelded joints in offshore strutures.
应用线性累积损伤准则与线弹性断裂力学方法,对近海结构管状焊接接头疲劳失效概率进行了分析与计算。
2.
The paper calculates the fatigue failure probability by using Monte carlo simulation method of important sampling, and compares with the direct Monte carlo method.
提出了用重要性抽样的MonteCarlo模拟法计算管节点的疲劳失效概率,并与直接抽样的MonteCarlo法进行了比较,结果表明:用重要性抽样法计算可大幅度地提高计算效
补充资料:疲劳生热试验
分子式:
CAS号:
性质:考察橡胶耐疲劳性能的一种试验。根据疲劳方式的不同可分为压缩疲劳生热、扭转疲劳生热、拉伸疲劳生热等多种形式。疲劳生热试验除要观察试样表面裂口增长情况外,对原试样还应测定其内部生热。橡胶疲劳生热性能是橡胶重要试验项目,尤其对轮胎而言,橡胶的疲劳生热是造成轮胎内部脱层、起鼓直至爆破的重要原因。
CAS号:
性质:考察橡胶耐疲劳性能的一种试验。根据疲劳方式的不同可分为压缩疲劳生热、扭转疲劳生热、拉伸疲劳生热等多种形式。疲劳生热试验除要观察试样表面裂口增长情况外,对原试样还应测定其内部生热。橡胶疲劳生热性能是橡胶重要试验项目,尤其对轮胎而言,橡胶的疲劳生热是造成轮胎内部脱层、起鼓直至爆破的重要原因。