1) NiAlMn high temperature shape memory alloy
NiAlMn高温形状记忆合金
2) high temperature shape memory alloy
高温形状记忆合金
1.
The research on martensite phase transition of Ti,Ni,Hf,Cu high temperature shape memory alloy;
TiNiHfCu高温形状记忆合金的马氏体相变研究
2.
The influence of Cu on martensite phase transition of high temperature shape memory alloy;
添加Cu对高温形状记忆合金马氏体相变的影响
3.
Considerable factors of developing high temperature shape memory alloys;
开发高温形状记忆合金应考虑的因素
3) high temperature Cu-based shape memory alloy
高温铜基形状记忆合金
1.
The recent developments of high temperature Cu-based shape memory alloy are reviewed.
本文概述了高温铜基形状记忆合金的最新研究进展。
4) low temperature SMA
低温形状记忆合金
5) Shape memory alloy
形状记忆合金
1.
Preparation of Single Crystal Cu-Al Based Shape Memory Alloy;
单晶Cu-Al系形状记忆合金制备研究
2.
Study of the TiNi shape memory alloy prepared through directional solidification;
定向凝固制备TiNi形状记忆合金的研究
3.
Transformation characteristics of Ti-50.2Ni shape memory alloy heat-treated in different processes;
不同热处理态Ti-50.2Ni形状记忆合金的相变特性
6) TiNi SMA
TiNi形状记忆合金
1.
Influence of Brazing Temperature on the Properties and Microstructure of TiNi SMA;
钎焊温度对TiNi形状记忆合金性能和组织的影响
补充资料：高温形状记忆合金
分子式：
CAS号：
性质：一般指高于普通形状记忆合金工作温度上限的形状记忆合金。高温形状记忆合金是在TiNi中加入Au，Pt或Pd取代Ni，用以提高相变点。其中有实用价值的是TiNi-Pd系。它有较高形状记忆应变(5％～6％)。随钯含量增加，形状恢复温度As最高可达到560℃。TiNi-Pd高温形状记忆合金的形状记忆效应机理与TiNi记忆合金类似，为热弹性马氏体相变时，相界/畴界作可逆运动，Ti50Nil3Pd37是TiNi-Pd系高温记忆合金的一种，形状恢复温度As为347℃，相变热滞为8℃，形状记忆应变为6％，室温和350℃断裂强度分别为1112MPa和918MPa。
CAS号：
性质：一般指高于普通形状记忆合金工作温度上限的形状记忆合金。高温形状记忆合金是在TiNi中加入Au，Pt或Pd取代Ni，用以提高相变点。其中有实用价值的是TiNi-Pd系。它有较高形状记忆应变(5％～6％)。随钯含量增加，形状恢复温度As最高可达到560℃。TiNi-Pd高温形状记忆合金的形状记忆效应机理与TiNi记忆合金类似，为热弹性马氏体相变时，相界/畴界作可逆运动，Ti50Nil3Pd37是TiNi-Pd系高温记忆合金的一种，形状恢复温度As为347℃，相变热滞为8℃，形状记忆应变为6％，室温和350℃断裂强度分别为1112MPa和918MPa。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。