1) rolling casting bonding
铸轧复合
1.
Nonhomogeneous diffusion thoughtto eliminate the embrittlementof steel- Al- 2 0 Sn inter- face was presented and realized by conducting steel- mushy Al- 2 0 Sn rolling casting bonding.
提出了消除钢 - Al- 2 0 Sn复合板复合界面脆化的非均匀扩散思想 ,并采用 Al- 2 0 Sn半固态浆料与钢板进行铸轧复合 ,实现了非均匀扩散 ,改变了复合界面结构 ,消除了复合板复合界面的脆化。
2) Double-Pour Roll
复合铸连轧辊
5) high Cr casting iron roll
高Cr复合铸铁轧辊
6) high Cr complex cast iron roll
高铬复合铸铁轧辊
1.
The material choice and i nfluence factors of work roll of 4 -h plate mill were simply discusse d In view of the existing problems of high Cr complex cast iron roll of plate mill of Handan Iron and S teel Co ,the paper analyzed the ca uses,and put forward the relevant improvement mea sure
简单论述了中板四辊轧机工作辊的材质选择原则及影响因素 ,对邯钢中板厂使用的高铬复合铸铁轧辊存在的问题及原因进行了分析 ,并提出了改进措施。
补充资料：薄板坯连铸连轧
薄板坯连铸连轧
thin slab CC-DR and CC-DHCR
baobanPi lianZhu lianzho薄板坯连铸连轧(thin slab CC一DR and CC-DHCR)薄板坯连铸后或连续铸轧后的直接轧制(continuous easting一direet rolling即ee一DR)和直接热装轧制(eontinuous easting一direet hot eharg rolling即CC一DHCR)，见带钢直接轧制。就大宗板带钢产品而言，薄板坯厚度以10一6omm为佳，这样经连铸连轧既可保证产品质量，又可有一定规模的产量，便于炼钢、连铸和轧钢生产能力的均衡匹配，并且显著简化工艺和设备，大大降低基建投资和生产成本，为中小型企业提供了成卷生产板带钢的有效途径。 薄板坯连铸连轧方式是从进一步节能、提高热轧板卷的成材率和增大热轧板卷重量的出发点产生的。薄板坯由于单位重量的表面积成倍增加，如果是用冷坯再加热轧制，其氧化铁皮损失也将成倍增加，并且还将使带钢卷重成倍减小，经济效益下降。因为实际生产中卷重增大，不仅可以提高产量、质量和成材率，而且也便于在轧制与精整以及深加工使用过程中高速自动化操作。因而，现代化热轧宽带钢厂有意将铸坯厚度由150~Zoomm增加到250一300mm。这就为薄板坯连铸一连轧发挥优越性提供了应用前景。 薄板坯连铸连轧工艺及轧机选型布置薄板坯连铸曾采用带有移动式结晶器的铸机，如履带式、双带式、单带式、轮带式及双辊式等连铸机进行试验研究，但仍未见有正式应用于大生产的成就。20世纪80年代以来，德国施罗曼一西马克(SMS)公司、曼内斯曼一德马克公司(MDH)及意大利达涅利(Danieli)公司等相继采用固定振动结晶器，在常规连铸机的基础上设计出新的薄板坯连铸机，进行薄板坯连铸获得成功。SMS公司采用漏斗形结晶器，上部展开呈椭圆形，这样一则可容纳浸入式水口，二则可保证铸坯无应力收缩。结晶器侧壁是平行的，铸坯宽度和断面可以改变，铸速可达5~6m/min，结晶器下支撑辊区长度只有5~6m，弯曲半径只有Zm左右，故铸机不高，厂房................可以矮。美国纽柯(Nucor)公司克劳福德维尔(Craw一案。若生产规模不大、年产70万t以下时，可选用图fordsvine)钢厂采用SMS公司开发的薄板坯连铸连轧‘的单流连铸后接可逆式单机或双机炉卷轧机(见炉技术(CsP)建立了一条年产80万t的带钢生产线，已卷轧机札制)。当年产50万t以下时，可采用图d的行于1989年投产。该厂由电炉炼钢，采用钢包冶金和保星轧机(见行星札机乳制)。