1) lead lanthanum zirconate stannate titanate
锆钛锡酸铅镧晶体
2) PLZST
锆钛锡酸铅镧
1.
Lead lanthanum zirconate titanate stannate(PLZST) perovskite single crystal with size of 2mm×(2mm×)2mm was grown by a flux method.
采用复合助熔剂技术,生长了完整、尺寸为2 mm×2 mm×2 mm的锆钛锡酸铅镧(简称PLZST)单晶。
3) PLZT
锆钛酸铅镧
1.
Preparation and Properties of PLZT Thin Films;
锆钛酸铅镧薄膜的制备与性能研究
2.
PLZT films have many significant applications in the ferroelectric integrated fields such as ferroelectric random access memories (FeRAM), dynamic random access memories (DRAM), etc.
锆钛酸铅镧铁电薄膜(PLZT)由于具备许多优良的铁电、介电性能、压电效应和电光效应等物理性能,被广泛的应用于动态随机存储器DRAM、非挥发性存储器FeRAM等铁电集成领域。
3.
Polycrystalline dysprosium (Dy) doped lanthanum zirconate-titanate (PLZT) ceramics with compositional formula [Pb0.
针对锆钛酸铅镧(PLZT)电光陶瓷在光调制器应用中存在工作电压偏高、场致滞后明显等不足,以镧系镝(Dy)元素对锆钛酸铅镧(Pb0。
4) PLZT
掺镧锆钛酸铅
1.
After being prolyzed and sintered, The PLZT ceramic fibers with a diameter of 25μwere obtained.
以乙酸铅、乙酸镧、乙酸氧锆和钛酸丁酯为原料,用溶胶-凝胶法制备了掺镧锆钛酸铅(PLZT)凝胶纤维。
5) lanthanum-modified lead zirconate titanate(PLZT)
掺镧锆钛酸铅(PLZT)
6) modification/lead lanthanum titanatezirconate ceramics(Abbr.PLZT)
改性/锆钛酸铅镧
补充资料：钛酸镧晶体
分子式：La2Ti2O7
CAS号：
性质：一种电光调制晶体。单斜晶结构，晶格常数1.30185nm，密度5.79g/cm3。熔点1790℃。居里点温度1500℃。自化极化沿c轴方向，光学上为双轴晶体。采用红外聚焦加热炉和浮溶技术生长单晶。为电光调制材料，用于制作压电振子和换能器。
CAS号：
性质：一种电光调制晶体。单斜晶结构，晶格常数1.30185nm，密度5.79g/cm3。熔点1790℃。居里点温度1500℃。自化极化沿c轴方向，光学上为双轴晶体。采用红外聚焦加热炉和浮溶技术生长单晶。为电光调制材料，用于制作压电振子和换能器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。