1) CaO-SiO_2-Al_2O_3-MgO-(CaF_2) slag
CaO-SiO2-MgO-Al2O3(-CaF2)渣系
2) CaO-Al2O3-SiO2-MgO-CaF2 Pentary Slag Serious
CaO-Al2O3-SiO2-MgO-CaF2五元渣系
3) CaO-SiO2-Al2O3-MgO-FetO slag
CaO-SiO2-Al2O3-MgO-FetO渣系
1.
The phosphorus capacity of CaO-SiO2-Al2O3-MgO-FetO slags was measured by equilibrating the slags in a molybdenum crucible with CO-CO2-Ar gas and Ag-0.
采用气-渣-金平衡法测定CaO-SiO2-Al2O3-MgO-FetO渣系的磷容量,用钼坩埚作为反应容器,Ag-0。
4) CaO-SiO2-MgO-Al2O3-FetO slag system
CaO-SiO2-MgO-Al2O3-FetO渣系
5) CaO SiO 2 CaF 2 flux
CaO-SiO2-CaF2渣系
6) CaO-SiO2-Al2O3-MgO-FetO slags
CaO-SiO2-Al2O3-MgO-FetO五元渣系
1.
The sulphur capacity of CaO-SiO2-Al2O3-MgO-FetO slags with fixed slag composition,at different temperature and under different gas pressure was measured using gas-slag equilibrium techniques.
采用气-渣平衡法,用铂坩埚作反应容器,CO-CO2-SO2-N2混合气体提供体系的氧分压和硫分压,测定了一定炉渣成分,不同温度和气氛条件下CaO-SiO2-Al2O3-MgO-FetO五元渣系的硫容量。
2.
The FetO activities of CaO-SiO2-Al2O3-MgO-FetO slags of fixed component was determined by the solid electrolyte cell: Mo|Mo+MoO2|ZrO2(MgO)|Fe+(FetO)+Ag|Fe under different temperatures and gas ratios.
采用Mo|Mo+MoO2|ZrO2(MgO)|Fe+(FetO)+Ag|Fe固体电解质电池测定不同温度和气氛条件下定组成CaO-SiO2-Al2O3-MgO-FetO五元渣系的FetO活度。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。