1) Vanadium corundum ceramics
钒刚玉瓷
1.
Results show that compress intensity of Vanadium corundum ceramics obtains great increase.
本文采用SHPB技术对钒刚玉抗弹陶瓷的动态力学性能进行了研究 ,结果表明钒刚玉瓷在动态条件下其强度得到了很大提高。
2) emerald alloyed abrasive
钒刚玉
3) ceramic corundum
陶瓷刚玉
1.
Granulation of ceramic corundum abrasives by dry process with planetary ball mill;
陶瓷刚玉磨料行星磨干法造粒研究
2.
Effect of sintering temperature on microstructure and mechanical property of ceramic corundum abrasives;
烧结温度对陶瓷刚玉磨料性能的影响
4) Corundum ceramics
刚玉陶瓷
1.
The applications of against-wear of corundum ceramics in the power plants were analysed by comparition, it is more effective than the other against-wear materials.
分析了刚玉陶瓷在火电厂防磨中的应用,和其它防磨材料比较,其防磨效果更佳。
5) ceramics corundum
陶瓷刚玉
1.
By using pressureless sintering technique,the ceramics corundum abrasives through the doping of MgO and SiO2 additives were prepared.
以氧化镁和氧化硅为烧结添加剂,利用无压烧结工艺制备了陶瓷刚玉磨料。
补充资料：钒磷铁矿提钒
钒磷铁矿提钒
extraction of vanadium from the bear vanadium phosphosiderite
和94％。fantintiekuang tifan钒磷铁矿提钒(extraetion of vanadium frombear vanadium phosphosiderite)以含钒磷铁矿为原料制取五氧化二钒的帆提取方法。主要包括钠化焙烧和湿法漫出两道作业。直接用作提饥原料的是含饥磷铁。 含钒磷铁是饥磷铁矿电炉生产单质磷和磷肥的副产品。钒磷铁矿分布在美国爱达荷、蒙大拿、怀俄明、犹他等州，含Pz05 24%~32%、V:O。0.267%~0.625%和少量的铬、镍和钥等。美国克尔麦吉(Kerr-MeGee)化学公司所用的含钒磷铁含饥3.26%~5 .2%、磷24.7%~26.6%、铁59.9%一68.5%、铬3.4%一5.7%、镍。.84%~1%。先将含钒磷铁磨至粒度小于。.42mm，配入1.4倍纯碱和。.1倍的食盐在回转窑中于1043~lo63K温度下焙烧，钒便转变成水溶性的钠盐。熔烧块在加热到沸腾的水中浸出，钒、铬、磷均溶入浸出液。浸出浆液经过滤处理。滤液冷却结晶析出磷酸钠晶体，用离心机分离。晶体中如仍含有钒和铬，可用水重溶后再结晶分离，直到获得合格的磷酸钠(NaaPO;)晶体产品。若Na3PO‘结晶母液含磷高于0. 989/L时则要加入CaclZ，使其生成磷酸钙沉淀，然后水解回收钒。随后往母液中加入硝酸铅，沉淀出铬酸铅。此工艺的钒、铬和磷的回收率分别为85%、65%