1) 95 chromium alumina ceramics
95铬刚玉瓷
2) Chromium corundum ceramics
铬刚玉瓷
3) High chromium corundum
高铬刚玉
1.
With high chromium corundum chosen as the refractory & aggregating material,and an phenol resin and PVB as the bonding agent,hereon,by applying orthogonal experiment to the above,consequently,an optimum ingredient ration is set up,conceming mould vanishing with alcohol base coating material for high manganese steel pieces to be casted.
选用高铬刚玉为耐火骨料 ,酚醛树脂和 PVB为粘结剂 ,通过正交试验 ,确定了高锰钢铸件消失模醇基涂料的最佳配比 ,考察了涂料的多种性能 ,并进行了生产验证。
2.
An optimum ingredient ration phosphate ceramic slurry was set up,by means of orthogonal experiment,with high chromium corundum chosen as the refractory and aggregating mateial,and aphosphate as the bonding agent.
选用高铬刚玉为耐火骨料、磷酸盐等为粘结剂、氧化镁为固化剂 ,通过正交试验 ,确定了磷酸盐陶瓷浆料的最佳配比 ,并考察了陶瓷浆料的多种性能、进行了精密铸件的生产应用。
4) chrome-corundum brick
铬刚玉砖
1.
In this paper a new technology of making chrome-corundum brick is introduced.
铬刚玉砖一般采用浇注成型或采用熔铸成型的工艺生产,但是这两种生产工艺分别存在着成本较高,生产效率较低、颗粒分布不够均匀等不足。
5) Chrome corundum brick
铬刚玉砖
6) chrome corundum
铬刚玉
1.
It introduces process control point of chrome corundum permeable brick and its application in smelting ferroalloys.
介绍了铬刚玉透气砖的生产控制要点和在铁合金精炼中的应用方法。
补充资料：alumina ceramics,95
分子式： Al2O3
CAS号：
性质：含量为95％(质量)的氧化铝陶瓷，主晶相为α-Al2O3，烧结温度在1650℃±20℃左右。主要性能：相对介电常数8.5～9.6，介电强度为15～18MV/m，体积电阻率1010～1012Ω·m，抗弯强度为280～350MPa，密度约3.5g/cm3。作为装置用陶瓷应用十分广泛。
CAS号：
性质：含量为95％(质量)的氧化铝陶瓷，主晶相为α-Al2O3，烧结温度在1650℃±20℃左右。主要性能：相对介电常数8.5～9.6，介电强度为15～18MV/m，体积电阻率1010～1012Ω·m，抗弯强度为280～350MPa，密度约3.5g/cm3。作为装置用陶瓷应用十分广泛。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条