1) Ni-Al thermal spray coating
Ni-Al喷涂层
2) Al/Ni coating
Al/Ni涂层
3) Ni-Al coating
Ni-Al涂层
1.
After annealing, the Ni-Al coatings have a good adherence with the substrate, and XRD shows that the coatings mainly composed of β-NiAl.
研究了Ni-Al涂层 对Ti-22Al-26Nb合金在800℃静态空气中氧化性能的影响。
4) Pd-Ni-Al coating
Pd-Ni-Al涂层
1.
Results show that the Pd-Ni-Al coatings have more adhesion than the simple aluminide coatings, and that the microstructural degradation of the Pd-Ni-Al coating is slower than that of the simple aluminide coating.
利用TGA、XRD、SEM以及金相等方法,研究了Pd-Ni-Al涂层在1 050℃的高温氧化行为。
5) (Ni,Pd)Al
(Ni,Pd)Al涂层
6) Ni-Cr-Al coating
Ni-Cr-Al涂层
1.
Influence of arc spraying parameters on the property of hardness of Ni-Cr-Al coating
热喷涂工艺对Ni-Cr-Al涂层硬度性能的影响
2.
The optimized process parameters of the arc spraying Ni-Cr-Al coating were obtained.
结果表明:喷涂电压、喷涂电流、雾化空气压力及喷涂距离对Ni-Cr-Al涂层孔隙率具有不同的影响,在优化的喷涂工艺参数下,Ni-Cr-Al涂层最小孔隙率可达5。
补充资料：Ni-Al microwave ferrite
分子式：Ni-Al
CAS号：
性质：又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上，用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%，磁性出现反常现象，这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035～0.145T，随铝量换量的增加而降低。居里温度155～440℃。铁磁共振线宽18.0～44.0kA/m(9kHz)。介电常数8.2～9.5。介质损耗角正切值（3～50）×10-4。采用电子陶瓷工艺，热压烧结或氮气氛烧结。适于制作高功率器件。
CAS号：
性质：又称镍-铝微波铁氧体。在镍旋磁铁氧体基础上，用三价铝离子置换一部分三价铁离子形成的镍-铝旋磁铁氧体。化学式为NiAlxFe2-xO4。当Alx的x值达约0.7%，磁性出现反常现象，这时材料已无实用值。按铝含量而分为0.1≤x≤0.4和0.7≤x≤1.0两类旋磁铁氧体。饱和磁化强度0.035～0.145T，随铝量换量的增加而降低。居里温度155～440℃。铁磁共振线宽18.0～44.0kA/m(9kHz)。介电常数8.2～9.5。介质损耗角正切值（3～50）×10-4。采用电子陶瓷工艺，热压烧结或氮气氛烧结。适于制作高功率器件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条