1) slurry erosion
浆体冲蚀
1.
Study of slurry erosion resistance of Cu-base and Ni-base flame spray welding coating;
Cu基、Ni基喷焊层材料的浆体冲蚀性能研究
2.
The slurry erosion and cavitation erosion resistance of the coatings have been investigated.
用氧乙炔焰喷焊法制备了NiCrSiB及其加入WC陶瓷颗粒的复合覆层材料,用光学显微镜分析了覆层的显微组织,并对覆层材料的浆体冲蚀和气蚀抗力进行了研究,用扫描电子显微镜对覆层表面气蚀破坏形貌进行了观察。
3.
The slurry erosion resistance of the test coatings has been investigated.
采用氧乙炔焰喷焊法制备 Ni基覆层材料及其加入 WC陶瓷颗粒的复合覆层材料 ,用光学显微镜分析覆层材料的金相组织 ,对覆层材料的浆体冲蚀抗力进行对比研究。
2) Slurry corrosion-erosion wear
浆体腐蚀冲蚀
3) Slurry erosion wear
浆体冲蚀磨损
1.
With the present situation and development of study of slurry erosion wear and slurry erosion resistance materials summarized, epoxy resin has many obvious merits such as high bonding strength, high strength and hardness and strong erosion resistance and has become erosion resistance adhesive coating of metal extensively.
通过国内外浆体冲蚀磨损以及抗浆体冲蚀磨损材料的研究现状及发展趋势研究资料的综述，我们了解到：环氧树脂因其粘结力强、强度和硬度高、耐腐蚀性能好等众多优点，目前已被广泛应用于金属材料表面的抗浆体冲蚀磨损胶粘层上。
4) slurry erosion
砂浆冲蚀
1.
Two different HVOF spray systems were used to prepare six WC–10Co–4Cr coatings on 0Cr13Ni5Mo stainless steel using three commercial powders, and the slurry erosion behavior of coatings and the substrate was investigated on a self-manufactured slurry pot erosion tester.
以2种不同的HVOF喷涂系统和3种商用粉末在0Cr13Ni5Mo基材上喷涂6种WC–10Co–4Cr涂层,用自行研制的料浆罐冲蚀设备对涂层和基材的砂浆冲蚀行为进行了研究,分析了显微结构和显微硬度对涂层冲蚀性能的影响及涂层冲蚀后的表面形貌。
5) slurry erosion
泥浆冲蚀
1.
Research on the slurry erosion resistance of coating produced by HVOF;
超音速火焰喷涂涂层耐泥浆冲蚀性研究
2.
Finally slurry erosion tests of various structured WC-12Co coatings and sprayed and fused Ni60 coating were carried out and their wear failure mechanisms of WC-12Co coatings were explored.
采用超音速火焰喷涂(HVOF)分别制备了纳米结构、双峰结构及微米结构WC-12Co金属陶瓷复合涂层,比较了不同结构WC-12Co涂层的组织结构及显微硬度,进行了不同结构WC-12Co涂层和Ni60喷熔层的泥浆冲蚀磨损试验,并探讨了它们的泥浆冲蚀机理。
6) erosion volume
冲蚀体积
1.
The experimental results show that the jet pressure rises and the rock erosion volume at unit horsepower increases rapidly when the jet pressure is lower than 150 MPa; but when the jet pressure reaches 150 MPa, it continues to rise and the rock erosion volume at unit horsepower decreases slightly.
实验结果表明,在射流压力低于150MPa时,随着射流压力升高,单位功率下的岩石冲蚀体积迅速增大,但当射流压力达到150MPa并进一步升高时,单位功率下的岩石冲蚀体积略有下降,150MPa时破岩效率最高;超高压喷嘴按前进的方式移动,破岩效果最佳;喷嘴移动速度小于2。
补充资料：冲蚀
冲蚀
erosion corrosion
ehongsh-冲蚀(erosion corrosion)金属材料表面与腐蚀流体冲刷的联合作用，而引起材料局部的金属腐性。在发生这种腐蚀时，金属离子或腐蚀产物因受高速腐蚀流体冲刷而离开金属材料表面，使新鲜的金属表面与腐蚀流体直接接触，从而加速了腐蚀过程。若流体中悬浮较硬的固体颗粒，则将加速材料的损坏。一般说来，流体的速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲刷腐蚀速度愈快。腐蚀介质流动速度又取决于流动方式:层流时，由于流体的粘度，在沿管道截面有一种稳态的速度分布;湍流时，破坏了这种稳态速度分布，这不仅加速了腐蚀剂的供应和腐蚀产物的迁移，而且在流体与金属之间产生切应力，能剥离腐蚀产物，从而加大了冲蚀速度。因此，在管道的拐弯处及流体进入管道或贮罐处容易产生这种破坏。另外，金属表面成膜的特征也可以影响冲蚀速度。硬的、致密的、连续的、粘附性强的膜冲蚀速度小，反之则大。抑制或减少冲蚀的措施是:选择耐蚀性和耐磨性好的材料;改变腐蚀环境如添加缓蚀剂，过滤悬浮固体粒子，降低温度，减小流速和湍流;采用栖牲阳极作阴机保护等。 (1陈树俊l)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。