1) Ni-Co-Mn alloy coating
镍钴锰镀层
1.
Contrasted to Ni-Co and Ni-Mn coating, the Ni-Co-Mn alloy coating had higher hardness and higher plasticity and much lower cobalt content.
提出了一种能很好地适应电镀金刚石工具要求的新型镀层即镍钴锰三元合金镀层 ,给出了新镀层的镀液配方 ,对比测量了镍钴锰镀层与目前广为采用的镍钴和镍锰镀层的硬度与韧性。
2) Ni Co Mn alloy coating
镍钴锰三元合金镀层
1.
The Ni Co Mn alloy coating is more suitable to manufacturing the matrix of electr.
提出了一种能很好适应电镀金刚石钻头要求的新型胎体材料即镍钴锰三元合金镀层 ,给出了新镀层的电镀液配方 ,对比测量了镍钴锰镀层与目前广为采用的镍钴和镍锰镀层的硬度与韧性。
3) Ni-Co electrodeposits
镍钴合金镀层
1.
Nano-crystalline Ni-Co electrodeposits were prepared using a complex additive containing phytic acid and organic amine salt.
采用植酸与有机胺盐复合添加剂制备了纳米镍钴合金镀层。
4) Fe-Co-Ni alloy coating
铁-钴-镍合金镀层
1.
In order to solve the repairing problem of worn sliding plate of airplane gun,the technology of brush plating for the Fe-Co-Ni alloy coating on the surface of high strength steel 18Cr2Ni4WA has been researched.
为了解决航炮磨损失效滑板的修复问题,研究了在18Cr2Ni4WA高强度钢表面刷镀铁-钴-镍合金镀层的工艺。
5) Ni-Co-Mn alloy
镍钴锰合金
6) LiMn1-x-yNixCoyO2
镍钴锰酸锂
补充资料：镍-镉扩散镀层
分子式：
分子量：
CAS号：
性质：就是先在零件上镀一层镍（12-15微米），然后在镍层上再镀一层镉（3-5微米），最后在335℃下进行1小时的扩散处理。形成镍镉金属间化合物的扩散层，熔点高，在500℃下具有良好的热稳定性，并具有良好的抗氧化性、耐热和耐蚀性。对基底材料抗应力腐蚀性能有很大提高，它适用于中温高强度钢、低合金钢和不锈钢的防护。对工作温度低于500℃的零件能提供良好的防护性能。过去这些零件采用镀镉防护，但隔层的使用温度只能在230℃以下，否则就不能起防护作用，并会引起一些材料的镉脆。改用镍镉扩散镀层，能满足防护要求。镍镉扩散镀层已应用于航空工业。
分子量：
CAS号：
性质：就是先在零件上镀一层镍（12-15微米），然后在镍层上再镀一层镉（3-5微米），最后在335℃下进行1小时的扩散处理。形成镍镉金属间化合物的扩散层，熔点高，在500℃下具有良好的热稳定性，并具有良好的抗氧化性、耐热和耐蚀性。对基底材料抗应力腐蚀性能有很大提高，它适用于中温高强度钢、低合金钢和不锈钢的防护。对工作温度低于500℃的零件能提供良好的防护性能。过去这些零件采用镀镉防护，但隔层的使用温度只能在230℃以下，否则就不能起防护作用，并会引起一些材料的镉脆。改用镍镉扩散镀层，能满足防护要求。镍镉扩散镀层已应用于航空工业。