1) mortar fluidity ratio
胶砂流动度比
1.
The mortar fluidity ratio and th e activity index of mortar at age of 7d ays and 28days were tested.
将不同颗粒群分布的矿渣、水泥按50%比例混合,测其胶砂流动度比和7d、28d抗折、抗压活性指数,应用Origin软件,以宏观性能指标为Z轴,水泥与矿渣D50差为X轴,水泥与矿渣混合样的粉体D50为Y轴,进行三维区域图分析。
2) mortar fluidity
胶砂流动度
1.
The mortar strength of coal gangue cement at age of 3days and 28 days, mortar fluidity and the water consumption of standard consistence of the coal gangue-cement paste were tested.
将不同细度的煤矸石、纯硅酸盐水泥按30%:70%混合, 测其胶砂流动度、净浆标准稠度用水量和 3 天、28天抗压强度。
2.
The mortar strength of coal gangue cement at age of 3d and 28d,mortar fluidity and the water requirement of normal consistency of the coal gangue-cement paste were tested.
将不同细度的煤矸石、纯硅酸盐水泥分别按30%和70%的比例混合,测其胶砂流动度、净浆标准稠度用水量和3d、28d胶砂抗压强度。
4) strength ratio of mortar
胶砂强度比
1.
For the same pozzolanic material, the varying trend of K a is similar to that of strength ratio of mortar as fineness was varied.
结果表明 ,Ka 与标准胶砂强度比具有较好的相关关系 。
5) strength ratio of recycled mortar
再生胶砂强度比
6) Mobility ratio
流动度比
补充资料：高化流动度试验仪
分子式：
CAS号：
性质：又称高化流动度试验仪，系日本高分子化学会定型的一种流动试验仪，属于柱塞加压式，毛细管挤出型。这种试验仪可适当选择负荷，自动记录柱塞下降量与时间的关系，并由此求出体积流速等流动特性。料筒温度在80～320℃范围内由电加热调节，并可以等速升温。负荷的选择范围为0.98～49.03MPa，通过改变负荷和毛细管的长径比，可获得较宽的剪切速率范围。这种定负荷式流动试验仪作为质量控制手段已得到广泛的应用。
CAS号：
性质：又称高化流动度试验仪，系日本高分子化学会定型的一种流动试验仪，属于柱塞加压式，毛细管挤出型。这种试验仪可适当选择负荷，自动记录柱塞下降量与时间的关系，并由此求出体积流速等流动特性。料筒温度在80～320℃范围内由电加热调节，并可以等速升温。负荷的选择范围为0.98～49.03MPa，通过改变负荷和毛细管的长径比，可获得较宽的剪切速率范围。这种定负荷式流动试验仪作为质量控制手段已得到广泛的应用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条