1) functionalized polyethylene wax
功能化聚乙烯蜡
1.
Intercalated masterbatches were prepared by melt compounding functionalized polyethylene wax with organic montmorillonites.
用两种不同改性剂与蒙脱土进行离子交换制得了两种有机蒙脱土 ,用功能化聚乙烯与有机蒙脱土进行熔融插层复合制备了功能化聚乙烯蜡 /有机蒙脱土插层复合母粒 ,用X -射线衍射、傅立叶红外光谱、热重分析、差示扫描量热和抽提实验等对所得有机蒙脱土和功能化聚乙烯蜡 /有机蒙脱土插层复合母粒的结构与性能进行表征。
2.
Organic montmorillonite filled polypropylene was prepared by blending functionalized polyethylene wax organic montmorillonite intercalated master batches with polypropylene.
将功能化聚乙烯蜡 /有机蒙脱土插层复合母粒与聚丙烯 (PP)共混 ,制备了有机蒙脱土填充的聚丙烯 。
3) oxidized polyethylene wax
氧化聚乙烯蜡
1.
Preparation of oxidized polyethylene wax emulsions;
氧化聚乙烯蜡微乳液的制备
2.
Composite based on polypropylene(PP) and sisal fiber(SF) containing oxidized polyethylene wax(OPE) is prepared by melt mixing and injection molding.
采用熔融共混与注塑成型的方法制备了聚丙烯/氧化聚乙烯蜡/剑麻纤维(PP/OPE/SF)复合材料,研究了氧化聚乙烯蜡(OPE)对复合材料力学性能的影响。
3.
The oxidized polyethylene wax(OPE) was modified with TEA and then emulsified for the steady cationic emulsion with the methods of phase conversion and compounding emulsifiers.
阳-非复合离子型氧化聚乙烯蜡乳液广泛应用于皮革涂饰、造纸、印染等领域,该文用三乙醇胺对氧化聚乙烯蜡进行酯化改性,再用相转变法和复合乳化体系对酯化改性的氧化聚乙烯蜡进行乳化,并对乳液性能进行检测分析。
4) Polyethylene Wax
聚乙烯蜡
1.
Polyethylene Wax and Colloidal Silica Shell Mold in Investment Casting;
聚乙烯蜡-硅溶胶熔模铸造工艺
2.
Solubility of Polyethylene Wax in Solvents;
聚乙烯蜡在溶剂中的溶解行为
3.
The study of polyethylene wax oxidation and graft modification
聚乙烯蜡氧化及接枝改性研究
5) PE-wax
聚乙烯蜡
1.
The rheological properties of HDPE 5000S containing lanthanides stearate or compounds of lanthanum stearate and lanthanides stearate /PE-wax blends were studied by means of constant rate and constant pressure rheometer.
利用恒速型、恒压型毛细管流变仪分别考察了镧系硬脂酸盐以及硬脂酸镧与聚乙烯蜡(PE-X)混合物对高密度聚乙烯(HDPE5000S)流变性能的影响。
6) Functionalizion of polystyrene
聚苯乙烯的功能化
补充资料：WE聚乙烯蜡
结构 [-CH2-CH2-]n
分子量1500～5000的乙烯聚合物统称聚乙烯蜡。WE型聚乙烯蜡又称高分子蜡，是一种聚烯烃合成高分子蜡。白色半透明，密度0.9，软化点96℃，粘度(140 ℃)550mPa·s。软化点虽高，而熔融粘度却很低，分散性、流动性好，与聚烯烃有良好的相容性。同时，还具有室温下抗湿性，耐化学药品性和优良电性能等特点。
用作增稠剂，参考用量约1％，使用时将10phr聚乙蜡加人到90phr甲苯中，加热90～100℃，迅速搅拌并使透明液冷却到60 ℃左右。加入冷甲苯100phr，迅速冷却成为分散液。然后继续搅拌冷却到30℃备用。WE型聚乙烯蜡也可用于制备热熔胶粘剂。贮存于阴凉、通风的库房内，远离火源。
分子量1500～5000的乙烯聚合物统称聚乙烯蜡。WE型聚乙烯蜡又称高分子蜡，是一种聚烯烃合成高分子蜡。白色半透明，密度0.9，软化点96℃，粘度(140 ℃)550mPa·s。软化点虽高，而熔融粘度却很低，分散性、流动性好，与聚烯烃有良好的相容性。同时，还具有室温下抗湿性，耐化学药品性和优良电性能等特点。
用作增稠剂，参考用量约1％，使用时将10phr聚乙蜡加人到90phr甲苯中，加热90～100℃，迅速搅拌并使透明液冷却到60 ℃左右。加入冷甲苯100phr，迅速冷却成为分散液。然后继续搅拌冷却到30℃备用。WE型聚乙烯蜡也可用于制备热熔胶粘剂。贮存于阴凉、通风的库房内，远离火源。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。