2) argon arc remelting
氩弧重熔
1.
Influence of argon arc remelting process on microstructure and properties of coating prepared by hot dipping aluminizing on surface Q235 steel
氩弧重熔对Q235钢热浸镀铝层组织和性能的影响
2.
The microstructure,wear resisting and abrasive mechanism of argon arc remelting area of alloyed casting iron camshaft is studied.
研究了合金铸铁凸轮轴氩弧重熔淬火后强化层的组织、耐磨性及磨损机理。
3.
This paper studied the causes of the early stage pitting on local areas and peeling off after 5000km drive in some grey cast iron camshafts which were treated by argon arc remelting.
分析研究了灰铸铁凸轮轴经氩弧重熔工艺处理后，约５０００ｋｍ 正常行驶后个别轴局部区域出现早期麻点与部分剥落而失效，结果证明早期失效的原因为氩弧重熔工艺不稳定所致。
3) argon shielded arc remelting
氩弧重熔
1.
WC composite wear-resistant coating were coated on the surface of 45# steel by means of the improved arc spraying technology, and then remelted by argon shielded arc remelting technology.
本文采用改进的电弧喷涂技术,以低碳钢为粘结剂,在45#钢表面喷涂WC-钢复合喷涂层,而后又使用氩弧重熔工艺对喷涂层重熔,制备了WC-钢复合熔覆层。
2.
WC-steel composite coatings were prepared on 45 steel material by arc spraying, and argon shielded arc remelting.
采用改进的电弧喷涂技术和氩弧重熔工艺在45钢基体上制备WC-钢基复合熔覆层。
4) tungsten inert-gas arc remelting
钨极氩弧重熔
5) metal argon arc welding
熔化极氩弧焊
1.
Based on practices of metal argon arc welding of red copper and low carbon steel, experimental analyses were carried out on some defects produced easily during welding of red copper and steel, such as crack, lack of fusion, and gas pore and so on.
通过紫铜与低碳钢的熔化极氩弧焊的生产实践 ,对铜钢焊接易产生裂纹、未熔合和气孔等缺陷进行了试验分析 ,并采用了合理的焊接工艺 ,提高了焊接接头的力学性能 ,保证了工件质
6) argon arc cladding
氩弧熔覆
1.
Investigation on argon arc cladding technology of Ni-based self-fluxing alloy;
氩弧熔覆镍基自熔合金的工艺研究
2.
Microstructure and wear resistance of argon arc cladding Ni-Mo-Zr-WC-B4_C composite coating
氩弧熔覆Ni-Mo-Zr-WC-B_4C复合材料涂层组织与耐磨性
3.
The investigation on the microstructure and properties of TiB/FeB reinforced Fe matrix composites coating by argon arc cladding
氩弧熔覆TiB/FeB增强Fe基复合涂层组织与性能研究