1) TiO 2 SiO 2 composite thin films
TiO2-SiO2复合膜
2) SiO2/TiO2 composite film
SiO2/TiO2复合膜
1.
In self-made ultraviolet photocatalytic reactor,the coal refuse sintering filter material was taken as the carrier,the SiO2/TiO2 composite film was taken as the catalyst,and the color removal from the film wastewater was taken as the research object to investigate the influences of the color,pH,aeration and illumination on its photocatalytic activity.
以煤矸石烧结滤料为载体,以SiO2/TiO2复合膜为催化剂,在自制的紫外光光催化反应器中,以去除胶片废水的色度为研究目标,考察了废水色度、pH、曝气/光照对SiO2/TiO2复合膜光催化活性的影响。
3) TiO2/SiO2 composite film
TiO2/SiO2复合膜
1.
TiO2/SiO2 composite film made by liquid deposition on the surface of coal fuse sintered filter material was used to study its photocatalytic degradation effect for DNNP waste water from a Huannan chemical plant.
采用液相沉积法在煤矸石烧结滤料表面制备了TiO2/SiO2复合膜,研究了TiO2/SiO2复合膜对淮南某化工厂DDNP废水的光催化降解效果。
4) Al2O3-SiO2-TiO2 composited membranes
Al2O3-SiO2-TiO2复合膜
5) TiO2/SiO2 compound
TiO2/SiO2复合
6) Al 2O 3-SiO 2-TiO 2-ZrO 2 composite membrane
Al2O3-SiO2-TiO2-ZrO2复合多孔膜
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。