1) TiO2-SiO2 composite particles
TiO2-SiO2复合粒子
1.
TiO2-SiO2 composite particles were prepared used sol-gel technology,which were characterized by FT-IR and SEM,TEM and calculated by x-ray quantitative analysis method.
采用溶胶-凝胶技术通过水解法在SiO2表面包覆纳米TiO2,制备出TiO2-SiO2复合粒子。
2) SiO2/TiO2 particles
SiO2/TiO2粒子
1.
In this paper, two methods for preparation of the SiO2/TiO2 particles were investigated.
本文采用两种工艺制备SiO2/TiO2粒子，方法一为以微乳法制备的SiO2粒子（100℃干燥）为核，在其上包覆TiO2层；方法二为采用溶胶-凝胶法制备的SiO2粒子（凝胶经24h老化）为核，通过溶胶-凝胶过程制备SiO2/TiO2粒子。
3) TiO2/SiO2 compound
TiO2/SiO2复合
4) nano TiO_2-SiO_2 composite particles
TiO2-SiO2纳米复合颗粒
1.
Shape memory polyurethane modified by nano TiO_2-SiO_2 composite particles was synthesized by prepolymer polymerization.
利用分子量为3 000的聚己内酯二元醇作为软段,二苯基甲烷二异氰酸酯作为硬段用预聚体法合成了形状记忆聚氨酯,在合成过程中原位加入经KH550表面处理后的TiO2-SiO2纳米复合颗粒,制备了新型形状记忆聚氨酯/TiO2-SiO2纳米复合颗粒复合材料。
5) TiO 2 SiO 2 composite thin films
TiO2-SiO2复合膜
6) SiO2/TiO2 composite film
SiO2/TiO2复合膜
1.
In self-made ultraviolet photocatalytic reactor,the coal refuse sintering filter material was taken as the carrier,the SiO2/TiO2 composite film was taken as the catalyst,and the color removal from the film wastewater was taken as the research object to investigate the influences of the color,pH,aeration and illumination on its photocatalytic activity.
以煤矸石烧结滤料为载体,以SiO2/TiO2复合膜为催化剂,在自制的紫外光光催化反应器中,以去除胶片废水的色度为研究目标,考察了废水色度、pH、曝气/光照对SiO2/TiO2复合膜光催化活性的影响。
补充资料：Tio2
钛的氧化物——二氧化钛，是雪白的粉末，是最好的白色颜料，俗称钛白。以前，人们开采钛矿，主要目的便是为了获得二氧化钛。钛白的粘附力强，不易起化学变化，永远是雪白的。特别可贵的是钛白无毒。它的熔点很高，被用来制造耐火玻璃，釉料，珐琅、陶土、耐高温的实验器皿等。
二氧化钛是世界上最白的东西， l克二氧化钛可以把 450多平方厘米的面积涂得雪白。它比常用的白颜料一—锌钡白还要白5倍，因此是调制白油漆的最好颜料。世界上用作颜料的二氧化钛，一年多到几十万吨。二氧化钛可以加在纸里，使纸变白并且不透明，效果比其他物质大10倍，因此，钞票纸和美术品用纸就要加二氧化钛。此外，为了使塑料的颜色变浅，使人造丝光泽柔和，有时也要添加二氧化钛。在橡胶工业上，二氧化钛还被用作为白色橡胶的填料。