1) cavitation-erosion behavior
空蚀磨损性能
2) erosion wear behavior
冲蚀磨损性能
1.
kW 3GQ 2/70 high pressure water jet cleaning device was used to evaluate the erosion wear behavior of a general hydraulic concrete with or without steel fiber.
选用 5 5 k W的 3GQ- 2 /70型高压清洗水射流装置作为水工混凝土的冲蚀磨损设备 ,考察了小角度条件下含沙高速水射流作用下混凝土材料的冲蚀磨损性能 。
3) wear corrosion resistance
腐蚀磨损性能
1.
In this paper, the wear corrosion resistance of several surface coatings, such as boronized-carburized- nitridied layer, tungsten carbide surfacing layer and high carbon & high chromium cast iron surfacing layer was investigated.
对B、C、N共渗层、碳化钨型硬质合金(D707)堆焊层、高碳高铬铸铁型硬质合金(D618)堆焊层等几种不同表面处理工艺,经相应热处理后的腐蚀磨损性能进行了研究。
4) erosive resistance
抗冲蚀磨损性能
1.
The erosive resistance of the composites layers were measured.
结果表明 ,碳化钨颗粒增强铁基表面复合材料具有良好的组织结构和优异的抗冲蚀磨损性能 ,与高铬铸铁相比 ,其抗冲蚀性是高铬铸铁的 3~ 4
6) Cavitations erosion
空蚀磨损
1.
The forms of cylinder failure and the role of cavitations erosion and corrosion on the course of cylinder failures were researched.
对K38发动机缸套失效进行了研究 ,并探讨了缸套失效原因、失效形式以及失效过程中空蚀磨损和腐蚀的作用。