2) impact corrosion and abrasion
冲击腐蚀磨损
1.
The impact corrosion and abrasion behavior of three steels for liner were investigated under different impact energy in ironstone slurry.
对三种湿磨衬板钢的冲击腐蚀磨损性能与机制的研究结果表明:冲击功增大,其磨损失重呈不同程度的增大;在2 0J冲击功下,三种钢的磨损失重相差不大;2 7J与3 5J时低碳高合金钢的磨损失重明显较小。
2.
The impact corrosion and abrasion properties of the low carbon alloy steels with different chromium content under the simulated working condition of metallurgical industry were investigated by MLD-10 impact-corrosion-abrasion tester.
2J冲击功下,低碳合金钢的冲击腐蚀磨损机制为:短时间内为累积变形引起的材料的浅层剥落,长时间后转变为多次塑变造成的表面硬化层的去除;在2。
3) corrosive impact abrasion
冲击腐蚀磨损
1.
Comparison of corrosive impact abrasion behavior between low carbon high alloy steel and high manganese steel;
低碳高合金钢和高锰钢冲击腐蚀磨损特性研究
4) corrosion and impact erosion-wear
腐蚀冲击磨损
5) corrosion and erosion-wear resisting
耐腐蚀冲击磨损
6) impact-corrosion-wear
冲击腐蚀磨损
1.
Investigation on impact-corrosion-wear property of two kind of steels;
两种钢冲击腐蚀磨损性能的试验研究
2.
A comparision of impact corrosion and wear praperties is made between high chromium cast iron and low corbon high alloy steel by the modified MLD-10 impact-corrosion-wear tester.
在改进后的MLD -10型冲击腐蚀磨损试验机上 ,对高铬铸铁和低碳高合金钢的耐冲击腐蚀磨损性能进行比较研究 ,通过不同条件下材料的失重、冲击磨损面的形貌、材料冲击端表层及亚表层的组织结构变化等来研究 2种材料的抗冲击腐蚀磨损性能 ,着重研究浆料性质、冲击功大小等对 2种材料抗冲击腐蚀磨损性能的影响。
补充资料：冲击腐蚀
分子式：
CAS号：
性质：属于磨耗腐蚀的一种腐蚀类型。是指金属表面与腐蚀流体之间由于高速相对运动而引起的金属损坏现象。一般而言，相对速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲击腐蚀的速度也愈快。由于金属离子或金属的腐蚀产物因受高速腐蚀流体强力冲刷作用而离开金属表面，促使新鲜的金属表面与腐蚀介质直接接触，加速腐蚀破坏的结果。
CAS号：
性质：属于磨耗腐蚀的一种腐蚀类型。是指金属表面与腐蚀流体之间由于高速相对运动而引起的金属损坏现象。一般而言，相对速度愈高，流体中悬浮的固体颗粒愈多、愈硬，冲击腐蚀的速度也愈快。由于金属离子或金属的腐蚀产物因受高速腐蚀流体强力冲刷作用而离开金属表面，促使新鲜的金属表面与腐蚀介质直接接触，加速腐蚀破坏的结果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。