烧损率,dead rate,在线英语词典,英文翻译,专业英语

1) dead rate

烧损率

The results of the experimouts show that the new technique may make the dead rate steady between 8%~9%,and improve the segregation in cast iron aluminium.

试验结果表明,应用钟罩压入新工艺可以使铝的烧损率稳定在8%—9%之间,并改善了铸铁铝的偏析缺陷。

2) burn-off rate

硼烧损率

3) Ti Burning Loss Rate

Ti烧损率

Effect of Slag Ingredient on Ti Burning Loss Rate and Ingot Surface Quality of High Temperature Alloy 0Cr15Ni25Ti2MoAlVB;

渣成分对高温合金0Cr15Ni25Ti2MoAlVB电渣重熔Ti烧损率和钢锭表面质量的影响

4) rare earth lost

稀土烧损率

5) Relative Melting Loss Rate

相对烧损率

6) burning loss

烧损

Some solutions are put forward by analyzing reasons of burning loss for the screwdown screw and nut on steckel mill.

通过对炉卷轧机的压下螺丝与螺母烧损的设备事故现象的分析,找出事故产生的原因,并提出了相应的解决方案。

In the paper,Mg regularities of distribution and effects of Mg burning loss on mechanical property of weld bead are researched during 5A06 alloy electro beam welding.

研究了5A06合金电子束焊接时熔池内Mg元素的分布规律及Mg元素烧损对焊缝力学性能的影响。

参考词条

钨极烧损挥发烧损烧损量电极烧损 Franklin烧损碳烧损烧损坑烧损泄漏元素烧损风口烧损感耦等离子体原子发射光谱依法治县

补充资料：烧损

烧损
fire waste

Sh0OSUn烧损(fi re waste)钢在高温状态下因氧化而造成的损耗。从锭坯到成品的整个生产过程中钢要经过多次加热，据测定，每加热一次约有0.5%一2.5%的钢被烧损。烧损不仅造成钢的直接损失，产生的氧化铁皮还降低钢的导热能力，侵蚀炉底耐火材料，恶化炉子操作条件，对轧件顺利咬入和钢材表面质量也产生不良影响。因此，减少金属烧损是钢加热过程中的重要间题。钢的烧损(氧化)过程主要是铁与炉气中的C02、02、H20发生化学反应的过程，其反应式如下: Fe+粤。，一Feo 2-‘一_ 3Fe+202一一Fe3O- ZFe:04+今。:一3FeZo3 -一‘一”’2一‘-一‘一J Fe+CO:一FeO+CO 3Fe+4COZ一Fe3O4+4CO 3FeO+COZ一FesO;+CO Fe十HZO一FeO+HZ 3Fe+4HZO一Fe3O4十4H2 3Fe+HzO一-今Fe3O;+Hz烧损与加热温度、加热时间、炉内气氛和钢的化学成分等因素有关。加热温度越高、高温下停留的时间越长、炉内氧化性气氛愈浓，则加热时的烧损愈多。因此减少烧损的主要措施是，在满足加热工艺的条件下，适当提高加热速度，缩短加热时间;控制炉内气氛，在保证燃料完全燃烧的条件下，减少过剩的空气并防止冷空气的吸入等。此外，采取保护性气体或用保护性涂料也能减少或防止钢的氧化。 (衷康)

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

首页 \| 翻译 \| 影视 \| 论坛 \| 索引降烧损防烧损烧损原因轴承烧损氧化烧损炭质烧损

1) dead rate 烧损率 1. The results of the experimouts show that the new technique may make the dead rate steady between 8%~9%,and improve the segregation in cast iron aluminium. 试验结果表明,应用钟罩压入新工艺可以使铝的烧损率稳定在8%—9%之间,并改善了铸铁铝的偏析缺陷。 2) burn-off rate 硼烧损率 3) Ti Burning Loss Rate Ti烧损率 1. Effect of Slag Ingredient on Ti Burning Loss Rate and Ingot Surface Quality of High Temperature Alloy 0Cr15Ni25Ti2MoAlVB; 渣成分对高温合金0Cr15Ni25Ti2MoAlVB电渣重熔Ti烧损率和钢锭表面质量的影响 4) rare earth lost 稀土烧损率 5) Relative Melting Loss Rate 相对烧损率 6) burning loss 烧损 1. Some solutions are put forward by analyzing reasons of burning loss for the screwdown screw and nut on steckel mill. 通过对炉卷轧机的压下螺丝与螺母烧损的设备事故现象的分析,找出事故产生的原因,并提出了相应的解决方案。 2. In the paper,Mg regularities of distribution and effects of Mg burning loss on mechanical property of weld bead are researched during 5A06 alloy electro beam welding. 研究了5A06合金电子束焊接时熔池内Mg元素的分布规律及Mg元素烧损对焊缝力学性能的影响。参考词条钨极烧损挥发烧损烧损量电极烧损 Franklin烧损碳烧损烧损坑烧损泄漏元素烧损风口烧损感耦等离子体原子发射光谱依法治县补充资料：烧损烧损 fire waste Sh0OSUn烧损(fi re waste)钢在高温状态下因氧化而造成的损耗。从锭坯到成品的整个生产过程中钢要经过多次加热，据测定，每加热一次约有0.5%一2.5%的钢被烧损。烧损不仅造成钢的直接损失，产生的氧化铁皮还降低钢的导热能力，侵蚀炉底耐火材料，恶化炉子操作条件，对轧件顺利咬入和钢材表面质量也产生不良影响。因此，减少金属烧损是钢加热过程中的重要间题。钢的烧损(氧化)过程主要是铁与炉气中的C02、02、H20发生化学反应的过程，其反应式如下: Fe+粤。，一Feo 2-‘一_ 3Fe+202一一Fe3O- ZFe:04+今。:一3FeZo3 -一‘一”’2一‘-一‘一J Fe+CO:一FeO+CO 3Fe+4COZ一Fe3O4+4CO 3FeO+COZ一FesO;+CO Fe十HZO一FeO+HZ 3Fe+4HZO一Fe3O4十4H2 3Fe+HzO一-今Fe3O;+Hz烧损与加热温度、加热时间、炉内气氛和钢的化学成分等因素有关。加热温度越高、高温下停留的时间越长、炉内氧化性气氛愈浓，则加热时的烧损愈多。因此减少烧损的主要措施是，在满足加热工艺的条件下，适当提高加热速度，缩短加热时间;控制炉内气氛，在保证燃料完全燃烧的条件下，减少过剩的空气并防止冷空气的吸入等。此外，采取保护性气体或用保护性涂料也能减少或防止钢的氧化。 (衷康) 说明：补充资料仅用于学习参考，请勿用于其它任何用途。