1) Mould-opening Temperature
开模温度
2) switch temperature
开关温度
1.
Three types of thermal sensitive polyurethane TSPU(a)、TSPU(b)and TSPU(c),were synthesized and their phase transition temperature of the soft segment(defined as switch temperature,Ts) were measured.
合成了三种温敏聚氨酯TSPU(a)、TSPU(b)和TSPU(c),并对其软段相的转变温度(即开关温度)进行了表征,同时研究了不同种类聚氨酯的相容性对共混体系开关温度阀值的影响。
3) initial rolling temperature
开轧温度
1.
The rolling results and performance analysis showed that the initial rolling temperature should be controlled from 1 100 ℃ to 1 180 ℃, If the temperature is higher than 1180 ℃, the rolled piece will be difficult to be bitted;if the temperature is below 1 100 ℃, the steel tend to thermal crisp and the head of rolled piece is easy to crack.
轧制结果及性能分析表明,开轧温度控制在1100～1180℃范围内较好,高于此温度范围轧制时会出现轧件打滑,咬入困难现象,温度低于此范围,钢容易发生热脆,轧件头部易开裂。
4) cogging temperature
开坯温度
1.
The ～1 300 ℃ cogging temperature and >20% deformation rate is good for Mo plate rolling.
而1300℃左右的开坯温度和20%以上的加工率将有利于钼板轧制生产的进行。
5) Temperature switch
温度开关
1.
The skip diaphragm temperature switch introduced in this paper is designed based on the characteristics of skip diaphragm andsheet bimetals.
本文介绍的跳跃式温度开关是跳跃膜片特性和双金属膜片温度特性的有机结合,即将普通的双金属片通过成形工艺加工成在温度作用下具有跳跃特性的双金属膜片,利用这种跳跃特性实现电源的接通和断开,达到温度控制的目的。
6) cracking temperature
开裂温度
补充资料：开尔文温度
以绝对零度作为计算起点的温度。即将水三相点的温度准确定义为273.16K后所得到的温度,过去也曾称为绝对温度。开尔文温度常用符号T表示;其单位为开尔文，定义为水三相点温度的1/273.16,常用符号K表示。开尔文温度和人们习惯使用的摄氏温度相差一个常数273.15，即T=t+273.15（t是摄氏温度的符号）。例如,用摄氏温度表示的水三相点温度为0.01°C，而用开尔文温度表示则为 273.16K。开尔文温度与摄氏温度的区别只是计算温度的起点不同，即零点不同,彼此相差一个常数,可以相互换算。这两者之间的区别不能够与热力学温度和国际实用温标温度之间的区别相混淆，后两者间的区别是定义上的差别。热力学温度可以表示成开尔文温度；同样，国际实用温标温度也可以表示成开尔文温度。当然，它们也都可以表示成摄氏温度。