1) chromium-bearing grey cast iron
含铬灰铸铁
1.
The chemical compositions of high carbide high chromium steel and chromium-bearing grey cast iron were optimized through orthogonally designed experiments which were carried out on a horizontal cantilevered centrifugal machine to compound the steel and cast iron by way of a centrifugal casting process.
通过正交设计实验优化得到了高碳高铬钢、含铬灰铸铁的最优成分;采用卧式悬臂离心实验机对高碳高铬钢/含铬灰铸铁进行离心复合·在复合成功的基础上,利用金相显微镜对不同实验条件下的复合界面进行了对比、分析·结果表明:经离心复合铸造,高碳高铬钢/含铬灰铸铁复合界面为结合紧密的复合层;复合试样经1080℃保温1h,水淬+500℃回火1h处理后,复合界面碳化物扩散更充分,但对复合界面宽度没有影响;浇注温度提高,复合界面宽度增加,当高碳高铬钢液浇注温度由1460℃提高到1480℃时,复合界面宽度增加了100μm
2) Gray cast iron containing Ti
含Ti灰铸铁
3) Cr-Cu micro-alloyed medium phosphorus grey iron
铬铜中磷灰铸铁
1.
needle-like microstructure should be prevented to appear in matrix and adopt Cr-Cu micro-alloyed medium phosphorus grey iron and lower C equivalent.
探讨了铬铜中磷灰铸铁活塞环(材料代号STD)的铸态组织分布规律,进而研究了STD活塞环铸态组织对活塞环的力学性能和摩擦磨损的影响,从而提出改进STD活塞环铸态组织的热稳定性和磨损性能的途径:要提高活塞环的热稳定性,必须防止基体组织出现针状组织;采用Cr和Cu微合金化中磷灰铸铁活塞环和降低活塞环的碳当量可提高活塞环的耐磨性。
4) high chromium cast iron containing B
含B高铬铸铁
5) Cr-alloyed white cast iron
含铬白口铸铁
1.
The effects of various modifying additives and modifying processes on the microstructure and properties of Cr-alloyed white cast irons were summarized.
总结了变质处理对含铬白口铸铁组织和性能的影响。
6) high chromium cast iron containing wolfram
含钨高铬铸铁
补充资料：灰铸铁
分子式：
分子量：
CAS号：
性质：含有片状石墨的铸铁。断口呈深灰色。具有优良的铸造、切削加工、抗磨、滑润、消振等性能，但强度较差，不能锻轧。常用在化工机械制造中。代号HT（huitie的缩写），加以最低抗拉强度σb及抗弯强度σw的数值。例如HT18－36，即表示σb≥176.4兆帕（18公斤力／毫米2），σw≥356.8I兆帕（36公斤力／毫米2）的铸铁。
分子量：
CAS号：
性质：含有片状石墨的铸铁。断口呈深灰色。具有优良的铸造、切削加工、抗磨、滑润、消振等性能，但强度较差，不能锻轧。常用在化工机械制造中。代号HT（huitie的缩写），加以最低抗拉强度σb及抗弯强度σw的数值。例如HT18－36，即表示σb≥176.4兆帕（18公斤力／毫米2），σw≥356.8I兆帕（36公斤力／毫米2）的铸铁。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。