1) Medium-chromium cast iron
中铬铸铁
1.
Influences of aging treatment,quenching temperature and tempering temperature on structure and property of medium-chromium cast iron were investigated.
研究了时效处理、淬火加热温度和回火温度对中铬铸铁组织性能的影响。
2.
The influences of types of modificators and their added volume fractions on the structure and properties of medium-chromium cast iron were investigated.
探讨了在相同试验条件下,变质剂种类及其加入量对中铬铸铁组织和性能的影响。
3.
The influence of Si/C ratio and speed of cooling on the as-c ast structure and properties of medium-chromium cast iron was investig ated.
研究了Ｓｉ／Ｃ和冷却速度对中铬铸铁铸态组织和性能的影响规律。
2) medium chrome cast iron
中铬铸铁
1.
Valence electron structure of medium chrome cast iron and its influence to medium temperature phase transformation;
中铬铸铁价电子结构及其对中温相变的影响
2.
The medium chrome-silicon cast iron(290Cr8Si2) is studied for increasing the M7C3content in eutectic carbide in medium chrome cast iron.
为提高中铬铸铁共晶碳化物中M7C3比例,研究了中铬硅铸铁(290Cr8Si2)。
3) medium chromium cast iron
中铬铸铁
1.
The results of study on the microstructure and thermal analysis of samples of the medium chromium cast iron with 2 79%C 7 17%Cr 0 48%Mn and various silicon content cast by metal mold and sand mold are: the fraction of (Fe,Cr) 7C 3 carbide increases with augmentation of silicon content and decrease of cooling rate.
对金属型和砂型铸造的含硅量不同的 2 79%C 7 17%Cr 0 48%Mn中铬铸铁试样进行了显微组织研究和热分析 ,结果表明 :(Fe ,Cr) 7C3 碳化物量随含硅量的增加和冷却速度的降低而增加。
4) middle Cr-Ni cast iron
中铬镍铸铁
5) Cr-Cu micro-alloyed medium phosphorus grey iron
铬铜中磷灰铸铁
1.
needle-like microstructure should be prevented to appear in matrix and adopt Cr-Cu micro-alloyed medium phosphorus grey iron and lower C equivalent.
探讨了铬铜中磷灰铸铁活塞环(材料代号STD)的铸态组织分布规律,进而研究了STD活塞环铸态组织对活塞环的力学性能和摩擦磨损的影响,从而提出改进STD活塞环铸态组织的热稳定性和磨损性能的途径:要提高活塞环的热稳定性,必须防止基体组织出现针状组织;采用Cr和Cu微合金化中磷灰铸铁活塞环和降低活塞环的碳当量可提高活塞环的耐磨性。
6) Medium chromium white cast iron
中铬白口铸铁
1.
： The Stracture and properties of medium chromium white cast iron which was cooled in different modes after 40% hot deformation are observed,measured and analyzed.
对经４０％热变形后不同方式冷却的中铬白口铸铁的组织与性能进行观察与测试，并对其进行分析，所得结果对热变形中铬白口铸铁的应用具有重要的指导意义。
2.
The microstructure of medium chromium white cast iron with 6% vanadium was observed and analyzed by use of SEM and TEM.
采用扫描电镜(SEM)、透射电镜(TEM)对含钒6%的中铬白口铸铁的组织进行了分析,采用恒电流电解的方法提取了铸铁中的碳化物相,用XRD进行了物相分析,分析得出含钒中铬白口铸铁组织中的共晶碳化物为M_7C_3型碳化物,而弥散分布的黑色颗粒是MC型碳化物。
补充资料：高铬铸铁
分子式：
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。
CAS号：
性质： 铬含量高的耐蚀耐热白口铸铁。依铬含量的不同，可分为铬含量26％～30％和32％～36％两类铸铁。在1000℃以上的氧化性气氛中，高铬耐热铸铁仍有好的抗氧化能力。有良好的强度以及较好的机械加工性能，但韧性较低，不宜用于温度急变场合。常用来制作加热炉炉底板、炉子传送链的构件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。