1) Cr-Containing Cast Iron with High Silicon
含铬高硅铸铁
2) high chromium-silicon wear-resistant cast iron
高铬硅耐磨铸铁
1.
The results of the ball-dropping impact-fatigue test and impact abrasiveness test showed that the impact-fatigue exfoliation resistance and anti-abrasiveness property of the developed as-cast and stress-relieving treated high chromium-silicon wear-resistant cast iron were better than the Cr15 martensite wearresistant cast Iron.
冲击疲劳落球试验和冲击磨损试验结果表明，研制的铸态去应力处理的高铬硅耐磨铸铁抗冲击疲劳剥落和抗冲击磨料磨损性能优于马氏体Ｃｒ１５耐磨铸铁；且高铬硅耐磨铸铁断面硬度均匀、生产成本较低。
3) high chromium cast iron containing B
含B高铬铸铁
4) high chromium cast iron containing wolfram
含钨高铬铸铁
5) high chromium cast iron
高铬铸铁
1.
Effects of compound modification on microstructure of hypereutectic high chromium cast iron;
复合变质对过共晶高铬铸铁凝固组织的影响
2.
Characteristic anlysis and material selection of high chromium cast iron for transflux parts of slurry pump;
渣浆泵过流件用高铬铸铁材料特性分析与选择
3.
A study on hardening behavior for high chromium cast iron 16Cr2MolCu under sub-critical treatment;
16Cr2Mo1Cu高铬铸铁在亚临界处理中硬化行为研究
6) high-chromium cast iron
高铬铸铁
1.
Cryogenic Treatment and the Properties of High-chromium Cast Iron;
深冷处理与高铬铸铁性能
2.
Research on optimization of cutter parameter and cutting specifications to high-chromium cast iron machining
高铬铸铁切削中刀具及切削用量优化研究
3.
The effect of Ti on the microstructure of the 4wt%C-20wt%Cr hypereutectic high-chromium cast iron was studied in this paper.
研究了不同的含Ti量对4C-20Cr(质量分数,%)过共晶高铬铸铁显微组织的影响。
补充资料：高硅铸铁
分子式：
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。