1) MgO-CaO castable
镁钙浇注料
2) Magnesia-based castable
镁质浇注料
1.
Magnesia-based castable was prepared with the weight ratio(aggregate: fines) of 70∶30.
以高纯镁砂(8~5mm,5~3mm,3~1mm)和电熔镁砂(≤1mm)为骨料,电熔镁砂细粉、α-Al2O3微粉、亚白刚玉粉、镁铝尖晶石细粉及uf-SiO2微粉为基质,按骨料∶细粉=70∶30进行配制镁质浇注料。
2.
The relationship between the physical properties of magnesia-based castable and the technical factors for preparing the castable such as grain size composition,amount of fine powders,binder,additives,and water has been investigated.
研究镁质浇注料的各种主要工艺因素(包括骨料配比、细粉、结合剂、微粉、外加剂和成型水量)与其物理性能之间的关系,进而获得镁质浇注料的较优化组成。
3.
The direct bond magnesia-chrome bricks which have been used in burning zone of cement rotary kiln were used,making fine powder which can replace the magnesia of the magnesia-based castable.
将水泥回转窑烧成带废镁铬砖经处理后制成细粉料,用它代替镁质浇注料中的镁砂原料,研究了废镁铬砖细粉的加入对SiO2微粉结合镁质浇注料烧结性的影响。
3) MgO-Al2O3 castable
镁铝浇注料
1.
The influence of MgO rich spinel content on porosity, bending strength and slag resistance of MgO-Al2O3 castable were studied in this article.
本文研究了富镁尖晶石细粉加入量对镁铝浇注料显气孔率、抗折强度和抗渣性能的影响。
4) magnesia castable
镁质浇注料
1.
To improve the good performance of magnesia castable,the effect of Si_3N_4 on the magnesia castable properties were studied.
为了提高镁质浇注料的耐用性,研究了Si_3N_4加入对镁质浇注料性能的影响。
2.
The slag resistance of magnesia castable without Sialon and with 5% bauxite-based β-Sialon was studied by revolution dipping meth-od at 1 600℃ for 10,15,20 and 25 minutes.
采用中频感应炉进行旋转浸渍法抗渣实验,研究了未加入和加入5%矾土基β-Sialon镁质浇注料在1600℃不同浸渍时间(分别为10,15,20,25min)条件下的抗渣性能。
5) Magnesia chrome castable
镁铬浇注料
6) alumina-magnesia castable
铝镁浇注料
1.
Effect of matrix composition on slag resistance of alumina-magnesia castable;
基质组成对铝镁浇注料抗渣性能的影响
2.
Results show that in order to improve the slag corrosion resistance and infiltration inhibition effect of the aluminamagnesia castable,SiO_2 and CaO content in the alumina-magnesia castable,especially in the binder has to be reduced and formation of the low melting mass between the brick layer and slag layer be inhibited as well.
利用SEM分析手段研究了铝镁浇注料的抗渣性能。
补充资料：纯铝酸钙水泥耐火浇注料
纯铝酸钙水泥耐火浇注料
pure calcium aluminate cement castable refractories
ehun IUsuangai shuini naihuo liaozhuliao纯铝酸钙水泥耐火浇注料(pure ealeiumaluminate eement eastable refraetories)用纯铝酸钙水泥作结合剂，用高档耐火原料作骨料和粉料，按比例配合成的可浇注耐火材料。(见耐火浇注料)此类浇注料具有较高的耐火度和荷重软化温度，力学强度高、耐磨性好、体积稳定、抗渣性好和抗还原性气体能力强等特点，最高使用温度可达1700~1800℃。 组成纯铝酸钙水泥浇注料的配比同普通铝酸钙水泥浇注杆一样，也是由耐火骨料、粉料、结合剂和外加剂组成的，不过所用的铝酸钙水泥纯度高，化学成分主要为A12O:和Cao，杂质含量很少。它是用工业氧化铝和纯的石灰石或方解石、或工业碳酸钙为原料，按一定比例混合磨细后，采用烧结法或电熔法而合成的。矿物组成主要是二铝酸钙(Cao·ZAlzo户和少量的一铝酸钙(Cao·A12O3).但也有一种电熔纯铝酸钙水泥，其矿物组成主要是铝酸一钙和少量的七铝酸十二钙(12CaO·7A12O3)，以及一定量的a一A1203掺合料、前者凝结硬化速度正常，初凝时间为lh左右，终凝为6、sh;而后者是一种快凝水泥，初凝为15~3师in，终凝在4h之内，此种水泥一般需加缓凝剂方可使用。 这类浇注料的耐火骨料和粉料通常采用特级矾土熟料，电熔或烧结刚玉、合成英来石、镁铝尖晶石、铬刚玉、铝铬渣等，粒度组成是根据使用条件和浇注料衬体厚度加以调整。最大粒度一般为5 mm。其骨料顺粒级配为5~3mm占45%~55%，3~lmm占25%~30%，小于lmm占20肠~25%。其粉料粒度组成为:小于0.o88mm的大于95%，其中小于0.o44mm的占30环。总的组成为耐火骨料占60%~70%，耐火粉料占15%~20%，纯铝酸钙水泥占10%~20%。加‘水量(外加)占8%~10%，可掺加微量减水剂，以减少用水量，改善流动性，提高致密度。 性能物理性能随所用的骨料和粉料的材质性能不同而异。如用刚玉骨料和粉料配制成的纯铝酸钙水泥浇注料养护3d后的耐压强度为40~50MPa。110℃，24h加热后密度为2.95~5.109/em，，气孔率为18写~20%，耐压强度为50~60MPa，线变化率为o%。2500℃，sh烧后的密度为2.90~3.059/em3、气孔率为17%~19%，耐压强度为60一80MPa，线变化率为十0.5%。其线变化率为正的，主要是水泥中的CaO与A1203反应生成六铝酸钙，发生体积膨胀所致. 应用纯铝酸钙水泥结合的浇注料应用范围较广。在冶金工业中，纯铝酸钙水泥耐火浇注料多数用作高温炉和高温装置的衬里。如用于钢水真空脱气装置的浸演管外衬，喷射冶金和吹氢处理用的整体喷枪和吹缸枪衬体，电炉顶三角区衬体，LF炉沪盖衬体等。在机械工业中，用于各种感应炉内衬材料。在石油化工工业中，用作催化裂化反应器的高温耐磨衬里等。 (李再耕)