1) Magnesia casting plate
镁质浇注板
2) Magnesia-based castable
镁质浇注料
1.
Magnesia-based castable was prepared with the weight ratio(aggregate: fines) of 70∶30.
以高纯镁砂(8~5mm,5~3mm,3~1mm)和电熔镁砂(≤1mm)为骨料,电熔镁砂细粉、α-Al2O3微粉、亚白刚玉粉、镁铝尖晶石细粉及uf-SiO2微粉为基质,按骨料∶细粉=70∶30进行配制镁质浇注料。
2.
The relationship between the physical properties of magnesia-based castable and the technical factors for preparing the castable such as grain size composition,amount of fine powders,binder,additives,and water has been investigated.
研究镁质浇注料的各种主要工艺因素(包括骨料配比、细粉、结合剂、微粉、外加剂和成型水量)与其物理性能之间的关系,进而获得镁质浇注料的较优化组成。
3.
The direct bond magnesia-chrome bricks which have been used in burning zone of cement rotary kiln were used,making fine powder which can replace the magnesia of the magnesia-based castable.
将水泥回转窑烧成带废镁铬砖经处理后制成细粉料,用它代替镁质浇注料中的镁砂原料,研究了废镁铬砖细粉的加入对SiO2微粉结合镁质浇注料烧结性的影响。
3) magnesia castable
镁质浇注料
1.
To improve the good performance of magnesia castable,the effect of Si_3N_4 on the magnesia castable properties were studied.
为了提高镁质浇注料的耐用性,研究了Si_3N_4加入对镁质浇注料性能的影响。
2.
The slag resistance of magnesia castable without Sialon and with 5% bauxite-based β-Sialon was studied by revolution dipping meth-od at 1 600℃ for 10,15,20 and 25 minutes.
采用中频感应炉进行旋转浸渍法抗渣实验,研究了未加入和加入5%矾土基β-Sialon镁质浇注料在1600℃不同浸渍时间(分别为10,15,20,25min)条件下的抗渣性能。
4) Alumina magnesia castable
铝镁质浇注料
5) magnesia-zircon-chome castable
镁锆铬质浇注料
补充资料：重质碳酸镁 ，碳酸镁
药物名称：碳酸镁
英文名：
别名： 重质碳酸镁 ，碳酸镁
适应症： 用于胃及十二指肠溃疡的治疗。
用量用法： 口服：每次０．５～１ｇ，每日３次。
注意事项： 有轻泻作用；可产生ＣＯ２气体，有严重溃疡病患者慎用。禁与酸性药物配伍。
规格： 散剂。
类别：抗酸及抗溃疡药
英文名：
别名： 重质碳酸镁 ，碳酸镁
适应症： 用于胃及十二指肠溃疡的治疗。
用量用法： 口服：每次０．５～１ｇ，每日３次。
注意事项： 有轻泻作用；可产生ＣＯ２气体，有严重溃疡病患者慎用。禁与酸性药物配伍。
规格： 散剂。
类别：抗酸及抗溃疡药
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条