1)  recrystallized SiC
重结晶碳化硅
2)  fine crystal silicon carbide
细结晶碳化硅
3)  silicon carbide whisker
碳化硅晶须
1.
The key process parameters for the double-heating synthesis of silicon carbide whiskers with carbon black and SiO2 powders as raw materials are studied.
双重加热法是低成本、大批量合成碳化硅晶须的新技术,合成温度低、合成时间短、生成率高。
2.
The heat conductive silicone rubber with vinyl endblocked polymethylsiloxane as basic gum and silicone nitride(Si_3N_4) of different particle sizes and silicon carbide whisker as fillers was prepared.
以甲基乙烯基硅橡胶为基胶,选用不同粒径氮化硅粒子和碳化硅晶须为填料制备了导热硅橡胶。
3.
The silicon carbide whiskers and platelets are ideal reinforcements of compound materials of ceramic,metal and resin.
碳化硅晶须和晶片都是陶瓷基、金属基、树脂基复合材料的理想增强体,与碳化硅晶须相比,有关碳化硅晶片制备与应用的报道相对较少。
4)  silicon carbide whiskers
碳化硅晶须
1.
All kinds of approach and the mechanism to synthesize silicon carbide whiskers are commented on , and the progress of silicon carbide whiskers at home and abroad is also reviewed.
比较详细地介绍了当前国内外碳化硅晶须的生长机理与制备方法,简要评述了对碳化 硅晶须研究的进展状况。
2.
Carbon nanotubes (CNTs) and silicon carbide whiskers (SiCw) are promising reinforcement materials for manufacturing metal or ceramic based composites.
在制备复合材料中,碳纳米管和碳化硅晶须易受到空气和基体材料侵蚀而失效。
5)  SiC Whiskers
碳化硅晶须
1.
The growth of SiC whiskers by in-situ on the surface of SiC foam ceramics;
泡沫碳化硅陶瓷表面原位生长碳化硅晶须
2.
Using silica micro-powder,quartz sand and kaolin as raw material of silicon,graphite with different particle size as raw material of carbon,Fe2O3、H3BO3 and NaCl as catalyst,SiC whiskers were synthesized by the carbothermal reduction reaction.
分别以SiO2微粉、石英砂和高岭土为硅源,用不同粒度的石墨为碳源,Fe2O3、H3BO3和NaCl作为催化剂,采用碳热还原法制备了碳化硅晶须。
3.
The dispersion of carbon black in silica sol and SiC whiskers synthesized by sol-gel method were studied.
本文研究了炭黑在硅溶胶中的分散以及溶胶-凝胶法制备了碳化硅晶须,同时也研究炭黑在酚醛树脂中的分散及各种改性树脂的制备,探讨了改性树脂对低碳镁碳砖性能的影响。
6)  silicon carbide platelets
碳化硅晶片
补充资料:重结晶碳化硅制品


重结晶碳化硅制品
recrystallized silicon carbide brick

飞花粼如德 成品 重结晶碳化硅砖的制造工艺流程重结晶碳化硅砖制造工艺要点:(l)级配必须能达到最大堆集密度,泥料成型压力必须保证获得大的体积密度。(2)烧成必须采用与李气哪绝的可达2500℃高温的电炉进行。温度在210Q℃以上,siC发生燕发凝结,导致无收缩的自结合结构。 用途重结晶碳化硅制品主要用作窗具,有节能、增加窑的有效容积、缩短烧成周期·提高窑的生产效率、经济效益高等优点,还可用作烧嘴喷嘴头、陶瓷辐射加热管、元件保护管(特别是用于气氛炉)等、 (郑安忠)chonglieJ!ng tanhuagui zhipin皿结晶碳化硅制品(reerystallizedsiliconearbide briek)以碳化硅为原料制成的破化硅与碳化硅直接结合的衬火制品。其特点是无第二相存在,由100%。一SIC构成,为20世纪80年代开发的新型节能窑具材料。重结晶碳化硅砖的性能(举例)·见表。 盆结晶碳化硅砖的性能乙 制造重结晶碳化硅用原料的化学组成如下:SIC99.5%,游离C 0.2肠,Fe 0.08%,游离51020.08%。制造重结晶碳化硅砖的工艺流程见图。