1) solid solutions Ce 1-x EuxO 2-δ
固溶体Ce1-xEuxO2-δ
2) (Ce_(1-x)Eu_xO_y) solid solution
Ce1-xEuxOy固溶体
1.
(Ce_(1-x)Eu_xO_y) solid solutions of different mole ratios(x=0.
采用溶胶凝胶法和微波技术制备了Ce1-xEuxOy固溶体,以甲烷催化燃烧为探针反应及XRD,BET和TPR对催化剂进行了表征。
3) Ce1-xPrxO2 solid solution
Ce1-xPrxO2固溶体
1.
A series of praseodymium-doped ceria,Ce1-xPrxO2 solid solution( 0≤x≤0.
结果表明:随着Pr掺杂量的增加,固溶体的氧空位浓度一致增大;Ce1-xPrxO2固溶体中Ce的价态为+4价,Pr离子以+3价的形式存在;样品的红度、色饱和度随Pr含量的增加呈先增后减趋势,当x=0。
4) Delta solid solution
δ固溶体
5) solid solution Ce0.8Eu0.2O2-δ
固溶体Ce0.8Eu0.2O2-δ
6) CexPd1-xO2-δ solid solution
CexPd1-xO2-δ固溶体
1.
Results of XRD indicated that CexPd1-xO2-δ solid solution was formed when the catalysts were calcined at 400-800 ℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000 ℃).
XRD结果表明,焙烧温度从400℃升高到800℃,有利于CexPd1-xO2-δ固溶体的形成。
补充资料：饱和固溶体
saturatedsolidsolution：溶质的含量相当于给定温度下处于平衡状态的最大量的固溶体；即能与该温度下过剩的溶质（相）共存的固溶体。