1) TiO_2 porous film
TiO2多孔性薄膜
1.
Photocatalytic degradation of low level formaldehyde in the gas phase was studied in a intermittent recirculation photocatalytic reaction system with TiO_2 porous film photocatalyst coated on stainless steel mesh.
采用不锈钢丝网负载TiO2多孔性薄膜光催化剂,在间歇式循环光催化反应系统中研究了气相中低浓度甲醛的光催化降解,考察了催化剂载体、催化剂镀膜次数、甲醛初始浓度和光源等因素的影响,并对光催化剂的稳定性进行了研究。
2.
TiO_2 porous film supported on stainless steel mesh as metal substrate was prepared by sol-gel technique with polyethylene glycol(PEG) as template.
采用溶胶-凝胶工艺,以聚乙二醇(PEG)为造孔剂,不锈钢丝网为金属基底,制备了TiO2多孔性薄膜。
2) porous TiO2 thin films
多孔TiO2薄膜
1.
The porous TiO2 thin films deposited on the surface of common glass surface were prepared from alkoxide solutions containing polyethylene glycol (PEG) by dip-coating technique.
配制了含不同分子量聚乙二醇的TiO2溶胶,采用浸渍提拉法在普通载玻片上制备了单、双层多孔TiO2薄膜。
3) porous TiO2 thin film
TiO2多孔薄膜
4) TiO2 porous nanometer thin films
TiO2多孔纳米薄膜
5) TiO2 porous thin film electrode
TiO2多孔薄膜电极
1.
TiO2 porous thin film on flexible ITO/PET substrate was prepared by screen printing and TiO2 porous thin film electrode was prepared by sintering at low-temperature.
采用丝网印刷技术在柔性基底ITO/PET上制备TiO2多孔薄膜,经过低温烧结得到TiO2多孔薄膜电极。
6) TiO_2 nanometer porous film
TiO2纳米多孔薄膜
补充资料：多孔性聚合薄膜
分子式：
CAS号：
性质：多孔性聚合薄膜是一种高分子薄膜材料，在聚合薄膜上分布有很多穿透性的微孔，孔径从0.025μm到14μm，分成多种规格。常被运用渗透、滤过等装置中。微孔总面积占薄膜总面积的80％，孔经大小均匀。多孔性聚合薄膜的种类有醋酸纤维膜，硝酸纤维膜，醋酸纤维与硝酸纤维混合酯膜，聚酰胺膜(polyamide，nylon 66)。聚四氟乙烯膜(polytetrafluo-rethylene)，聚碳酸酯膜(polycarbonate)，聚砜膜(polysulfone)等。中国已有上述各种薄膜生产。如纤维素混合酯膜，将原料溶于溶剂，并加入致孔剂和一些附加剂，在一定的温度与湿度条件下，用流涎法制备。