1) porous TiO_2 film
多孔TiO2膜
2) TiO_2 porous film
TiO2多孔膜
1.
The TiO_2 porous film was prepared by constant voltage anodic oxidation on the surface of pure titanium using sulphuric acid and hydrofluoric acid as electrolytes.
以硫酸和氢氟酸为电解液,采用恒压阳极氧化方式,在TA1表面获得多孔TiO2膜,并研究了电解液对TA1表面TiO2多孔膜形态和晶型的影响规律。
3) TiO2 porous film
TiO2多孔膜
1.
The effect of the different electrolyte morphology of TiO2 porous film on pure titanium was studied in this work.
电解液在阳极氧化中发挥着重要作用,本文着重研究了不同电解液对钛箔表面生成TiO2多孔膜形态和成分的影响规律。
4) porous TiO2 thin films
多孔TiO2薄膜
1.
The porous TiO2 thin films deposited on the surface of common glass surface were prepared from alkoxide solutions containing polyethylene glycol (PEG) by dip-coating technique.
配制了含不同分子量聚乙二醇的TiO2溶胶,采用浸渍提拉法在普通载玻片上制备了单、双层多孔TiO2薄膜。
5) porous TiO2 thin film
TiO2多孔薄膜
6) TiO_2 porous film
TiO2多孔性薄膜
1.
Photocatalytic degradation of low level formaldehyde in the gas phase was studied in a intermittent recirculation photocatalytic reaction system with TiO_2 porous film photocatalyst coated on stainless steel mesh.
采用不锈钢丝网负载TiO2多孔性薄膜光催化剂,在间歇式循环光催化反应系统中研究了气相中低浓度甲醛的光催化降解,考察了催化剂载体、催化剂镀膜次数、甲醛初始浓度和光源等因素的影响,并对光催化剂的稳定性进行了研究。
2.
TiO_2 porous film supported on stainless steel mesh as metal substrate was prepared by sol-gel technique with polyethylene glycol(PEG) as template.
采用溶胶-凝胶工艺,以聚乙二醇(PEG)为造孔剂,不锈钢丝网为金属基底,制备了TiO2多孔性薄膜。
补充资料：多孔膜
分子式：
CAS号：
性质： 指每平方厘米含有一千万至一亿个孔，孔隙率占总体积70％～80％，孔径均匀，孔径范围在0.02～20μm之间的分离膜。当膜的孔径大于5nm时称为微孔膜(microporous membrane)；孔径在1～5nm时称细孔膜(fine-pored membrane)，包括超滤膜和反渗透膜。