1) Reserved elongation at break
断裂伸长率保留率
2) Elongation At Break Retention
断裂伸长保留率
3) Retention rate of elongation at break
拉伸断裂伸长率保留率
4) retention of elongation
伸长保留率
5) elongation at break
断裂伸长率
1.
The tensile strength,elongation at break,notch impact strength and flexural strength of PBT were increased by 12%,100%,1.
1份时,PBT的拉伸强度提高12%,断裂伸长率提高100%,冲击强度提高10%,弯曲强度提高5%,综合力学性能最好。
2.
The tensile strength and the elongation at break were 23 MPa and 460% when the compound plasticizing agent were made up of(1.
在此条件下,PVA217流延膜的各种性能较好,拉伸强度约为23 MPa,断裂伸长率约为460%。
3.
The resin could be cured at ambient temperature and the tensile strength and elongation at break of the cured resin were 20 MPa and 106% respectively,which could be used to make high flexible products or could be also added in normal unsaturated polyester resins to improve their anti-impact properties and elongation at break.
介绍了1种新型二异氰酸酯改性不饱和聚酯,该树脂可以室温固化,固化后树脂的拉伸强度和断裂伸长率分别可达20 MPa和106%。
6) breaking elongation
断裂伸长率
1.
The relations between breaking strength/breaking elongation and core-spun degree are analyzed.
分析了断裂强力、断裂伸长率与包覆度的关系。
2.
Furthermore,if the lighting illumination is strong enough,the breaking elongation and glass tr.
本文通过对不同光照条件下得到的可见光固化及过氧化物固化的乙烯基酯(VLC)树脂的弯曲、拉伸性能和玻璃化转变温度及残留苯乙烯含量的比较研究,发现只要保证可见光照射的照度和光照量,VLC树脂可见光固化物性能和过氧化物固化物性能相当,高照度光源照射下双酚型VLC-760浇铸体的断裂伸长率及玻璃化转变温度会有明显提高。
3.
The results showed that with the the increase of outside force velocity,the tension yield strength of PVC increased,but its breaking elongation decreased.
结果表明:PVC的拉伸屈服强度随外力作用速度的提高而提高,断裂伸长率却随之下降。
补充资料：断裂伸长率
分子式：
CAS号：
性质：又称断裂伸长率。材料在拉伸断裂时的伸长变形量。一般用拉伸断裂时试样上标线间距离的增加百分率来表示。符号为ε，是度量塑性大小的一种数据。塑性材料的伸长率极限较大，脆性材料的伸长率极限较小。
CAS号：
性质：又称断裂伸长率。材料在拉伸断裂时的伸长变形量。一般用拉伸断裂时试样上标线间距离的增加百分率来表示。符号为ε，是度量塑性大小的一种数据。塑性材料的伸长率极限较大，脆性材料的伸长率极限较小。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条