1) Intumescent Flame Retardant PP
膨胀型阻燃聚丙烯
1.
Study on Intumescent Flame Retardant PP Reinforced by Nylon;
用尼龙 6(PA6)代替部分季戊四醇 (PT)作成炭剂 ,制得了膨胀型阻燃聚丙烯 (IFR PP) ,讨论了PA6对IFR PP的力学性能、阻燃性能、热稳定性和流变行为的影响。
2.
Study on Intumescent Flame Retardant PP/Nylon/Nano-meter Montmorillonite Blend;
用尼龙 6(PA6)代替季戊四醇 (PT)作为成炭剂组成的膨胀型阻燃聚丙烯 (PP)有熔滴、阻燃效果差的缺点 ,加入纳米蒙脱土 (nano MMT)作为阻燃剂的协效剂后可克服以上缺点。
3) Intumescent flame retardant
膨胀型阻燃
1.
Ammonium polyphosphate(APP)-pentaerythritol(PT)- melamine( M) systems have been chosen as an intumescent flame retardant(IFR),chlorination rubber as matrix resin to prepare flame resistant coating.
以多聚磷酸铵(APP)_季戊四醇(PT)_三聚氰胺(M)为膨胀型阻燃体系(IFR),氯化橡胶为基材树脂,制备阻燃涂料。
2.
The effect of the intumescent flame retardant system on ABS/PA6(80/20) alloys was studied.
以聚磷酸铵(APP)为酸源,利用ABS/PA6合金中PA6为炭源对ABS/PA6合金进行膨胀型阻燃研究,探讨了不同成炭协效剂与APP复配对合金阻燃性能的影响,这些成炭协效剂包括季戊四醇笼状磷酸酯(PEPA),热塑性酚醛树脂(TPPFR),环氧树脂(E-44)和分子筛4A。
4) fire-resistance expanded polystyrene panel
阻燃型膨胀聚苯板
5) intumescent fire retardant
膨胀型阻燃剂
1.
Polypropylene(PP) was fire retarded with a novel phosphorus,nitrogen and sulfur containing intumescent fire retardant(IFR),1,4-(O,O-diethyl thiophosphoryl imine) benzene (DTPB) which was synthesized by using phosphorus thiochloride,dehydrated alcohol and p-phenylenediamine.
以三氯硫磷、无水乙醇、对苯二胺为原料所合成的新型含磷、硫、氮的膨胀型阻燃剂(IFR),1,4-(O,O-二乙基硫代磷酰亚胺基)苯(DTPB)对聚丙烯(PP)进行阻燃,用热重法(TG)和差示扫描量热法(DSC)对阻燃PP的热性能进行了研究,利用氧指数仪测定了阻燃PP的极限氧指数(LOI)值,当阻燃剂含量为28%,LOI值为37。
2.
The typical system of intumescent fire retardant APP(ammonium polyphosphate) PER(pentaerythritol) was used to retard the combustion of low density polyethylene(LDPE) and the factors which influence the properties and the thermal degraded behaviour of intumescent fire retarded LDPE were discussed.
采用膨胀型阻燃剂—聚磷酸铵和季戊四醇 (APP/PER)体系对低密度聚乙烯 (LDPE)进行阻燃。
3.
The status of intumescent fire retardant developed was summaried by pentaerythritol and its derivatives, and heir the direction of development was prospected.
本文综述了以季戊四醇及其衍生物为炭源研制的膨胀型阻燃剂的发展状况,并对其今后的发展方向进行了展望。
6) Intumescent flame retardant
膨胀型阻燃剂
1.
The flame retardance and pyrolytic properties of cotton fabrics finished with intumescent flame retardant;
膨胀型阻燃剂整理棉织物的阻燃及热裂解性能
2.
Application of Melamine in Intumescent Flame Retardant and Flame Retardant Plastics;
三聚氰胺在膨胀型阻燃剂及阻燃塑料中的应用
3.
Application of intumescent flame retardants in fibers and textiles;
膨胀型阻燃剂在纤维及纺织品上的应用
补充资料：阻燃聚丙烯
分子式：
CAS号：
性质：以聚丙烯树脂与定量阻燃剂、改性添加剂、防老剂在高速混合器内混合，经双螺杆挤出机共混，而后经造粒、切粒、包装成产品。产品为白色颗粒。有优良的阻燃性、耐热性、耐冲击性和电绝缘性能。拉伸强度28MPa。相对伸长率30%。弯曲强度50MPa。热变形温度105℃。老化寿命150℃时为1000h。用于各种要求阻燃并且强度好、寿命长的电子电器零部件。
CAS号：
性质：以聚丙烯树脂与定量阻燃剂、改性添加剂、防老剂在高速混合器内混合，经双螺杆挤出机共混，而后经造粒、切粒、包装成产品。产品为白色颗粒。有优良的阻燃性、耐热性、耐冲击性和电绝缘性能。拉伸强度28MPa。相对伸长率30%。弯曲强度50MPa。热变形温度105℃。老化寿命150℃时为1000h。用于各种要求阻燃并且强度好、寿命长的电子电器零部件。