1) intumescent paints
膨胀型阻燃涂料
1.
A intumescent paints with good adhesion for PP board was prepared by proper choice of resins,solvents, additives and flame retardants etc.
通过表面处理和选择合适的树脂、溶剂、助剂、膨胀型阻燃剂等,制备出用于PP板表面的膨胀型阻燃涂料。
4) Intumescent flame retardant
膨胀型阻燃
1.
Ammonium polyphosphate(APP)-pentaerythritol(PT)- melamine( M) systems have been chosen as an intumescent flame retardant(IFR),chlorination rubber as matrix resin to prepare flame resistant coating.
以多聚磷酸铵(APP)_季戊四醇(PT)_三聚氰胺(M)为膨胀型阻燃体系(IFR),氯化橡胶为基材树脂,制备阻燃涂料。
2.
The effect of the intumescent flame retardant system on ABS/PA6(80/20) alloys was studied.
以聚磷酸铵(APP)为酸源,利用ABS/PA6合金中PA6为炭源对ABS/PA6合金进行膨胀型阻燃研究,探讨了不同成炭协效剂与APP复配对合金阻燃性能的影响,这些成炭协效剂包括季戊四醇笼状磷酸酯(PEPA),热塑性酚醛树脂(TPPFR),环氧树脂(E-44)和分子筛4A。
5) intumescent coatings
膨胀型涂料
6) intumescent fire retardant
膨胀型阻燃剂
1.
Polypropylene(PP) was fire retarded with a novel phosphorus,nitrogen and sulfur containing intumescent fire retardant(IFR),1,4-(O,O-diethyl thiophosphoryl imine) benzene (DTPB) which was synthesized by using phosphorus thiochloride,dehydrated alcohol and p-phenylenediamine.
以三氯硫磷、无水乙醇、对苯二胺为原料所合成的新型含磷、硫、氮的膨胀型阻燃剂(IFR),1,4-(O,O-二乙基硫代磷酰亚胺基)苯(DTPB)对聚丙烯(PP)进行阻燃,用热重法(TG)和差示扫描量热法(DSC)对阻燃PP的热性能进行了研究,利用氧指数仪测定了阻燃PP的极限氧指数(LOI)值,当阻燃剂含量为28%,LOI值为37。
2.
The typical system of intumescent fire retardant APP(ammonium polyphosphate) PER(pentaerythritol) was used to retard the combustion of low density polyethylene(LDPE) and the factors which influence the properties and the thermal degraded behaviour of intumescent fire retarded LDPE were discussed.
采用膨胀型阻燃剂—聚磷酸铵和季戊四醇 (APP/PER)体系对低密度聚乙烯 (LDPE)进行阻燃。
3.
The status of intumescent fire retardant developed was summaried by pentaerythritol and its derivatives, and heir the direction of development was prospected.
本文综述了以季戊四醇及其衍生物为炭源研制的膨胀型阻燃剂的发展状况,并对其今后的发展方向进行了展望。
补充资料：膨胀型防火涂料
分子式：
CAS号：
性质：通过形成泡沫炭化层以阻挡外部热源的一类防火涂料。成膜后，常温下是普通的漆膜。在火焰或高温下，涂层发生膨胀炭化，形成一个比原来膜厚度大几十倍甚至上百倍的不易燃的海绵状炭质层，使外界火源与基材隔绝，从而起到阻燃作用。通常以基料、发泡料、成炭剂、脱水成炭催化剂、防火添加剂、无机颜填料、辅助剂等制成。这类漆遇小火不燃，离火自熄，具有防延燃性。广泛应用于建筑、车辆、仓库、电器、包装等。
CAS号：
性质：通过形成泡沫炭化层以阻挡外部热源的一类防火涂料。成膜后，常温下是普通的漆膜。在火焰或高温下，涂层发生膨胀炭化，形成一个比原来膜厚度大几十倍甚至上百倍的不易燃的海绵状炭质层，使外界火源与基材隔绝，从而起到阻燃作用。通常以基料、发泡料、成炭剂、脱水成炭催化剂、防火添加剂、无机颜填料、辅助剂等制成。这类漆遇小火不燃，离火自熄，具有防延燃性。广泛应用于建筑、车辆、仓库、电器、包装等。